1) Silica Gel Encapsulated by Polystryrene
聚苯乙烯包覆硅胶微球
3) poly(styrene-divinylbenzene) coating
聚(苯乙烯-二乙烯苯)包覆
1.
The benzoyl peroxide was used as initiator to make poly(styrene-divinylbenzene) oligomer to coat onto the surface of glass fiber,resulting in poly(styrene-divinylbenzene) coating fiber.
以过氧化苯甲酰为引发剂,将苯乙烯-二乙烯苯交联低聚物包覆在玻璃纤维表面,得到聚(苯乙烯-二乙烯苯)包覆纤维,然后用浓硫酸将聚(苯乙烯-二乙烯苯)包覆纤维磺化,制备强酸性离子交换纤维。
4) Poly(ethylvinyl benzene-10-divinylbenzene)beads
聚苯乙烯-二乙烯苯微球
5) polystyrene microspheres
聚苯乙烯微球
1.
Factors influencing size of polystyrene microspheres in dispersion polymerization;
分散聚合反应中影响聚苯乙烯微球粒径的因素
2.
Evaporation self-assembly method, which is used to assemble sub-micrometer polystyrene microspheres, is presented in this paper.
建立了一种组装亚微米级聚苯乙烯微球的方法,称作蒸发自组装法。
3.
Monodisperse polystyrene microspheres were prepared by dispersion polymerization in ethyl alcohol reaction media using polyvinylpyrrolidone (PVP) as steric stabilizer and 2,2-azobisizobutyronitrile (AIBN) as initiator in a suitable condition.
以聚乙烯基吡咯烷酮 (PVP)为分散剂 ,无水乙醇为反应介质 ,偶氮二异丁腈为引发剂 ,采用分散聚合方法 ,制备出球形度良好的单分散聚苯乙烯微球。
6) Polystyrene microsphere
聚苯乙烯微球
1.
Micron monodispersed crosslinked polystyrene microspheres were prepared by suspension polymerization in glucose aqueous solution with poly(vinyl alcohol)(PVA)as stabilizer.
采用葡萄糖水溶液为分散介质,加入稳定剂聚乙烯醇,经悬浮聚合法合成了微米级单分散交联聚苯乙烯微球,考察了葡萄糖含量、苯乙烯用量、引发剂用量、稳定剂用量和交联剂用量对微米级单分散交联聚苯乙烯微球粒径大小及其分布的影响。
2.
Three-dimensionally ordered macroporous SiO_2 materials(3DOM SiO_2) were successfully synthesized by using colloid crystal template which was assembled by sedimentation of polystyrene microsphere.
以聚苯乙烯微球(polystyrenemicrosphere)自然沉积形成的胶体晶体作模板,将以正硅酸甲酯制备的SiO2溶胶填充到模板间隙中,原位形成凝胶,最后通过焙烧除去模板,得到三维有序大孔SiO2。
3.
Three-dimensional ordered macroporous CeO2 materials(3DOM CeO2) were successfully synthesized by using colloid crystal template which was assembled by rapid centrifugation of polystyrene microspheres.
以聚苯乙烯微球(polystyrene microsphere)高速离心组装的胶体晶体为模板,以Ce(NO3)3。
补充资料：聚苯乙烯/聚乙烯共混物
分子式：
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。