1) VIBROMOLD
自振式结晶器
1.
Application of hydraulic VIBROMOLD in billet casting at Baotou Steel;
液压自振式结晶器在包钢小方坯连铸中的应用
2) Mold Oscillation
结晶器振动
1.
The temperature at the meniscus during continuous casting was measured under mold oscillation by model experiments.
设计了连铸结晶器弯月面处传热模拟实验,测量了在结晶器振动情况下弯月面处的温度,发现该处的温度随着结晶器的振动而产生周期性的变化。
2.
The high temperature mechanical property of steel 20G is measured,the secondary cooling equipment is revamped and process parameters such as superheat,mold oscillation,secondary cooling water distribution are adjusted.
为提高产能,对圆坯连铸机进行了提拉速工业试验,测定了试验钢种20G的高温力学性能,对二冷设备进行了改造,对钢水过热度、结晶器振动参数及二冷配水等工艺参数进行了调整。
3.
In order to study the effect of mold oscillation on initial shell stress state,stress simulation model was set up by using the Marc software.
为研究结晶器振动对初生坯壳应力状态的影响,利用Marc软件建立了结晶器内初生凝壳的应力计算模型,分析了振动过程中凝壳上应力和应变的分布规律。
3) Mould Oscillation
结晶器振动
1.
Influence of Mould Oscillation Parameters on Surface Quality of Concasting Billet;
结晶器振动参数对连铸坯表面质量的影响
2.
The Software Development of Mould Oscillation Detection and Analysis System;
结晶器振动检测与分析系统软件开发
3.
The influence of mould oscillation on surface quality of continuous cast slabs is introduced.
论述了结晶器振动对连铸坯表面质量的影响 ,归纳出一些对生产实际和科研都有指导价值的结
4) amplitude of mold
结晶器振幅
1.
BG510L,SW400 and BG420CL,and makes some suggestions such as reducing water budget match and amplitude of mold vibration,adjusting secondary cooling model,reducing the sulfur content and controling the speed of casting to control this defect and improve the quality of continuous casting slab.
针对本钢炼钢厂BG510L、SW400、BG420CL等包晶钢板坯表面横裂缺陷率较高的状况,对其成因进行分析研究,提出了降低结晶器水量配比、减小结晶器振幅、调整二冷配水模型、降低钢中氮硫含量和稳定拉速等改进措施,从而控制了包晶钢表面横裂纹的发生,提高铸坯质量。
5) mould hydraulic oscillation
结晶器液压振动
1.
In terms of equipment,measures taken include small pitch,split roll,continuously bending and straightening,soft reduction segments,mould hydraulic oscillation,mould electromagnetic brakes,fine control over mould level,longer vertical section of the caster,ladle slag detection,big concavity tundish and tundi.
在设备方面采用了小辊密排、分节辊布置、连续弯曲和连续矫直,轻压下扇形段,结晶器液压振动,结晶器电磁制动,高精度的结晶器液面控制,较长的铸机垂直段,大包下渣检测,大容量中间包及对中间包吹氩;在工艺方面采用先进的一冷、二冷技术,动态轻压下;其他管理方面采用质量管理和对铸机进行定期检查维护等措施。
6) crystallizer vibro-bench
结晶器振动台
补充资料：Howard式结晶器
分子式：
CAS号：
性质：是一种古老的连续式结晶器，可进行晶体的生长与分级。如图所示，这种装置由三个圆锥体垂直连接而成，各圆锥部分均各自独立地用水冷却。热浓溶液自底部送入，在结晶器内上升，冷却水与溶液逆向流动。在以上升流为主的中段，晶体处于流态化状态，晶体的生长与成核均在此段进行。长大的晶体与液流逆向沉降，由流速最大的结晶器底部取出。结晶器最上部的断面积很大，因而液体流速变小，可防止晶体溢流。由于液体的上升流速不能太大，故冷却面上有晶体析出，传热速度下降，是其缺点。