1) Al-24%Si piston alloy
Al-24%Si活塞合金
1.
The Al-24%Si piston alloy was modified with single RE,P and Sr,and binary RE+P or RE+Sr or P+S along with ternary P+RE+Sr,the ternary P+RE+Sr modification agent with was found to have excellent effect.
采用混合稀土(RE)、磷、锶对过共晶Al-24%Si活塞合金进行单一、二元、三元变质处理,得到了变质效果优良的P+RE+Sr三元复合变质剂。
4) Al-Si alloy
Al-Si合金
1.
Simulation of mold filling and solidification on gravity casting of Al-Si alloy(A357);
Al-Si合金(A357)重力铸造充型及凝固过程模拟
2.
Electromagnetic Separation of Magnetic Impurity Particles in Al-Si Alloy Melt;
Al-Si合金熔体中磁性杂质颗粒的电磁分离
3.
Effects of high magnetic fields on the distribution of Si in solidified structures of Al-Si alloy;
强磁场对Al-Si合金凝固组织中硅分布的影响
5) Al-Si alloy
Al-Si 合金
1.
Micro-arc oxidation coatings were prepared on Al-Si alloy surface using own made micro-arc oxidation device.
采用自制的微弧氧化装置,在 Al-Si 合金表面制备了微弧氧化涂层,在对涂层进行表征的基础上,进行了其往复滑动的摩擦磨损性能研究。
6) Al Si alloy
Al-Si合金
1.
Fe and Ni with high melting points can be melted directly into the surface of Al Si alloy by Argon arc.
利用氩弧将高熔点的铁、镍直接熔入 Al-Si合金表面 ,经重熔后获得组织均匀的表面合金化层 ,合金化层的深度约 5 mm。
2.
Mn is added into Al Si alloy containing Fe, then cast into sample and weld wire.
在含 Fe的 Al-Si合金中加入 Mn元素 ,铸成试样和焊丝 。
3.
The testing results showed that a significant modifying effect can be achieved in eutectic Al Si alloy in die casting by the addition of w(RE) being 0.
8%的稀土对共晶Al-Si合金具有良好的变质效果 ,而在 960～ 10 60℃下的过热处理能使 RE变质后的共晶 Al-Si合金中的 Si相进一步细化 ,从而获得良好的凝固组织。