1) Ti-Si intermetallic compound
钛硅金属间化合物
2) Ti-Al intermetallic
钛铝金属间化合物
1.
Ti-Al intermetallic matrix composite with interpenetrating Al2O3 whiskers was fabricated in situ through heat-treating the prefabricated pieces consisting of titanium,aluminum and external reactant powders at partial-oxidizing atmosphere.
以金属钛粉、铝粉及添加剂为原料压制成预制体,通过石墨与氧化铝混合粉对预制体的覆埋实现气氛保护并进行热处理,使其原位合成氧化铝纤维增强钛铝金属间化合物复合材料。
2.
Ti-Al intermetallic matrix composite with interpenetrating Al2O3 whiskers w as fabricated in-situ by heat-treating the prefabricated pieces consisted of titanium, aluminum and columbium pentoxide powder in non-oxidizing atmospher e.
以金属钛粉、铝粉和五氧化二铌粉末压制成预制体,通过石墨与氧化铝混合粉对预制体的覆埋实现气氛保护并进行热处理,使其发生化学反应原位合成氧化铝晶须增韧钛铝金属间化合物复合材料。
3) Ti-Ni Inter-metallic compound
钛镍金属间化合物
4) Fe-Si intermetallic compound
铁硅金属间化合物
1.
In order to confirm the excellent thermal shock resistance of Fe-Si intermetallic compound thimble,we have compared SiC sintered pipes' thermal shock resistance with thimbles fabricated of different binders in molten aluminum,and analyzed fractography by means of scanning electronic microscopy.
为了证实铁硅金属间化合物套管良好的抗热震性能,本文将不同胶粘剂成型的铁硅金属间化合物套管,以及SiC冷静压烧结管在熔融铝液中进行了抗热震性对比测试,并用扫描电镜分析了断口形貌。
5) Ni 3(SiAl)
镍三硅铝金属间化合物
6) cast TiAl intermetallic alloy
铸造钛铝金属间化合物合金
补充资料：钛铝金属间化合物
分子式：
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。
CAS号：
性质：钛铝原子比为1：1的金属间化合物。为以面心立方晶格为基础的L10型有序结构。密度小，为3.91g/cm3。使用温度达1000℃。具有良好的高温比强度和比刚度。优异的抗氧化性能。可采用高温合金的制备方法制取。理想的航天航空用轻量型高温材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。