1) Mo-Zr alloy
Mo-Zr合金
1.
Mo-Zr alloy were fabricated by powder metallurgy process,the effect of the adding forms of Zr and its content on the tensile property and microstructure of the alloy were studied.
采用粉末冶金方法制备Mo-Zr合金,研究了Zr的添加方式及添加量对Mo的拉伸性能和显微组织的影响。
2) Mo-Ti-Zr alloy
Mo-Ti-Zr合金
1.
Influence of (Mo, Zr, Ti)_xO_y particles on mechanical properties and microstructure of rotary forging Mo-Ti-Zr alloy;
(Mo,Zr,Ti)_xO_y粒子对旋锻Mo-Ti-Zr合金性能和组织的影响
3) Zr Al Ni Cu Mo alloy
Zr-Al-Cu-Mo合金
4) TLM(Ti-3Zr-2Sn-3Mo-15Nb) alloy
TLM(Ti-Zr-Sn-Mo-Nb)合金
5) Ti-Fe-Mo-Mn-Nb-Zr alloy
Ti-Fe-Mo-Mn-Nb-Zr合金
6) Zr-4 alloy
Zr-4合金
1.
Fretting Corrosion Property of Zr-4 alloy in Na_2SO_4 Solution;
Zr-4合金在Na_2SO_4溶液中的微动腐蚀磨损特性
2.
The microstructures and polarization curves of Zr-4 alloy treated by laser surface niobium alloying,electron beam surface niobium alloying and niobium ion implantation alloying were studied.
通过对Zr-4合金进行激光表面铌合金化、电子束表面铌合金化和铌离子注入,分析了表面铌合金化后锆合金表层的显微组织,并测定了表面合金化后锆合金在酸性溶液中的极化曲线。
3.
The hot deformation behaviors of Zr-4 alloy under the temperature range of 750～950 ℃and strain rate range of 0.
在Gleeble-1500热模拟机上对Zr-4合金进行了热压缩试验,研究了其在750~950℃和0。
补充资料：Mo-Ti-Zr-C alloy
分子式：
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。