1) non-aluminum killed steel
非铝镇静钢
1.
The reason for nozzle clogging in ladle in casting of non-aluminum killed steel treated by CAS-OB refining furnace is analyzed.
分析了CAS-OB精炼炉处理的非铝镇静钢在连铸浇铸过程中发生钢包水口堵塞的原因,通过优化CAS-OB操作工艺,解决了钢包水口堵塞问题。
2) Al-killed steel
铝镇静钢
1.
Practice on process of Argon bubbling and deoxidation by addition of Al in Al-killed steel ladle;
铝镇静钢钢包吹氩定氧加铝工艺实践
2.
Absorption Ability of Casting Mold Powder for Al-Killed Steels to Al_2O_3 Inclusion;
铝镇静钢连铸保护渣对Al_2O_3夹杂物的吸收能力
3.
The effect of boron on precipitation of AlN and MnS in low-carbon Al-killed steel;
硼对低碳铝镇静钢中AlN、MnS析出的影响
3) aluminium killed steel
铝镇静钢
1.
Against the problem of silicon increased much more in refining production of low-silicon low-sulfur aluminium killed steel for cold-rolling with LF furnace in No.
针对邯钢三炼钢厂冷轧用低硅低硫铝镇静钢LF炉精炼生产增硅严重的问题,对其限制性环节进行分析后,制定了新的LF精炼工艺,使供冷轧用料的钢水合格率明显提高。
2.
Deoxidising high quality aluminium killed steel with silicon-free ferroaluminium-manganese instead of purd aluminium exists some problems such as the production cost is increased,steel quality is impaired etc.
高品质的铝镇静钢以无硅铝锰铁合金代替纯铝脱氧应用后存在成本增加和影响钢质量等问题。
4) Al killed steel
铝镇静钢
1.
Analysis and disposal of factors affecting the pouring result of Al killed steel;
影响铝镇静钢可浇性的因素分析及所采取的措施
5) aluminium-killed steel
铝镇静钢
1.
Based on it, the model of controlling aluminium-killed steel by adding aluminium was set up.
根据铝脱氧的反应机理，进行定氧加铝试验，得出在不同残氧量时的加铝量控制标准，并在此基础上建立了铝镇静钢的定氧加铝模型，在简化加铝量计算的同时提高了钢中[Al]控制的准确度。
2.
The plastic strain ratio, including conventional strain ratio and instantaneous strain ratio, of an aluminium-killed steel sheet was measured at various tensile strain levels by tentile test.
通过单轴拉伸实验测算了深冲用铝镇静钢在不同拉伸应变水平下的塑性应变比，包括常规应变比ｒ~ｃ和瞬间应变比ｒ~ｉ。
6) LCAK steel
低碳铝镇静钢
1.
The behavior of non-metallic inclusions of LCAK steel produced with BOF-LF-FTSC process route was studied by means of metallographic electrolysis,EDS and SEM,and the source,amount and sized distribution were revealed.
采用全氧分析、金相观察、扫描电镜(SEM)、电子探针(EDS)、大样电解等手段,对唐钢BOF-LF-FTSC工艺生产低碳铝镇静钢非金属夹杂物行为进行了全面系统的研究,找出了夹杂物的类型、来源、数量及尺寸大小在不同工序的变化规律,提出了改善薄板坯洁净度的建议。
2.
An investigation was made on cleanness and non-metallic inclusions of LCAK steel produced with BOF-ANS-CC production route.
采用转炉— ANS精炼—连铸工艺生产低碳铝镇静钢 ,ANS处理后钢液 T[O ]含量在 (35～ 5 6 )×10 - 6 之间 ,铸坯 T[O]含量在 2 5× 10 - 6 左右。
补充资料：GCr15钢中的大型非金属夹杂物(铝酸盐)×500
GCr15钢中的大型非金属夹杂物(铝酸盐)×500
GCrl5钢中的大型非金属夹杂物(铝酸盐) ×500
说明：补充资料仅用于学习参考，请勿用于其它任何用途。