1) liquid-phase direct precipitation
液相直接沉淀法
1.
Preparation of nanosized SnO_2 by liquid-phase direct precipitation method;
液相直接沉淀法制备纳米SnO_2
2) direct precipitation
直接沉淀法
1.
Study on producing of nanometer ZnO by direct precipitation method;
直接沉淀法制备纳米氧化锌工艺研究
2.
Preparation and identification of ZnO ultrafine powder by direct precipitation;
直接沉淀法制备ZnO超细粉末及其性质测定
3.
Characteristics of ZnO Nanoparticle Prepared by Direct Precipitation;
直接沉淀法制备纳米ZnO及表征
3) Direct precipitation method
直接沉淀法
1.
Ultrafine cobalt oxalate (CoC2O4·2H2O) powder was prepared by the direct precipitation method using cobalt sulfate (CoSO4), oxalic acid (H2C2O4).
以硫酸钴(CoSO4)和草酸(H2C2O4)为原料,采用直接沉淀法制备超细草酸钴(CoC2O4·2H2O)粉体。
2.
Nanometer zinc oxide powder has been prepared by direct precipitation method using zinc electrolyte as raw material from a factory in Xiangxi and Na2CO3 as precipitator.
以湘西某电解锌厂的锌电解液为原料,用碳酸钠为沉淀剂,采用直接沉淀法制备纳米氧化锌粉体。
3.
Superfine-sized magnesium oxide powders were synthesized by direct precipitation method.
通过正交实验法,研究了直接沉淀法合成超细氧化镁的诸因素对粒径和收率的影响,得到了最佳的工艺条件:反应物MgCl2浓度为1。
4) liquid phase precipitation method
液相沉淀法
1.
Nano manganese oxide was prepared by the liquid phase precipitation method,and characterized by XRD and TEM.
采用液相沉淀法制备了纳米氧化锰,通过色谱分析其脱硫效率,并通过X射线衍射(XRD)和透射电镜(TEM)对粉末样品的组成、结构、粒径和形貌进行了表征。
5) liquid-phase precipitation method
液相沉淀法
1.
CuSCN nano-particles were prepared in CuSO_4 solution by liquid-phase precipitation method using Na_2SO_3 as reducing agent and NaSCN as precipitating agent.
以无机盐CuSO4为原料 ,Na2 SO3 做还原剂 ,NaSCN为沉淀剂 ,采用液相沉淀法制备了CuSCN纳米颗粒 ,制备的CuSCN产品粒度在 70～ 90nm左右 ,产品粒度较均匀。
2.
In order to get the compact mica glass-ceramic sintered body,the powder precursor of complex oxide was prepared by liquid-phase precipitation method,the powder was treated by the two-step crystallization heat treatment to get machinable mica glass-ceramic powder containing fluorophlogopite(NaMg3AlSiO3O10F2) as the main crystalline phase.
为了获得致密的云母玻璃陶瓷烧结体,采用液相沉淀法制备出分散性好的复合氧化物前驱粉体,粉体经两步法晶化热处理后得到主晶相为氟金云母(NaMg3AlSiO3O10F2)的可加工云母玻璃陶瓷粉体。
6) precipitation method
液相沉淀法
1.
Compared two methods,purity LSO powders is synthesized without high temperature calcinations by precipitation method,while the raw materials remained after high temperature by mixing solid oxides method.
将氯化镥溶液滴加至硅酸钠溶液中制备出的沉淀,经过滤、陈化及烘干后对其进行XRD成分及SEM显微形貌的分析,结果表明粉体除少量杂质外,其主要成分都是由硅酸镥构成,而经烘干研磨后的粉体颗粒呈球形,将采用液相沉淀法与固体混合焙烧法所制备出的两种粉体进行了对比发现,采用前者可以不经高温煅烧就可以得到较纯硅酸镥,而后者在较高温度下煅烧后仍有大量原料残余,而且从颗粒尺寸、粉体形状以及烧结性能上来液相法制备出的粉体看都优于固相法。
补充资料：直接沉淀法
直接沉淀法是制备超细微粒广泛采用的一种方法，其原理是在金属盐溶液中加入沉淀剂，在一定条件下生成沉淀析出，沉淀经洗涤、热分解等处理工艺后得到超细产物。不同的沉淀剂可以得到不同的沉淀产物，常见的沉淀剂为：nh3•h2o、naoh、(nh4)2co3、na2co3、(nh4)2c2o4等。
直接沉淀法操作简单易行，对设备技术要求不高，不易引入杂质，产品纯度很高，有良好的化学计量性，成本较低。缺点是洗涤原溶液中的阴离子较难，得到的粒子粒经分布较宽，分散性较差。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条