1) pentaerythritol phosphate
季戊四醇型磷酸酯
2) Pentaerythritol Biphosphate
季戊四醇型双磷酸酯
1.
Study on Synthesis and Application of Pentaerythritol Biphosphate Fire Retardant;
季戊四醇型双磷酸酯阻燃剂的合成及应用研究
4) polymeric pentaerythrityl phosphate
聚季戊四醇磷酸酯
1.
)first in the absence of organic solvent,and then an oligomer polymeric pentaerythrityl phosphate was synthesized in yield 79% from PDD and hydroquinone(1equiv.
以季戊四醇、三氯氧磷为原料,采用无溶剂法首先合成了季戊四醇二磷酸酯二磷酰氯(PDD),n(季戊四醇)n∶(三氯氧磷)=1 5∶,收率为84%;然后以PDD和对苯二酚为原料,乙腈为溶剂,三乙胺为缚酸剂,在氮气氛围下合成了低聚阻燃剂聚季戊四醇磷酸酯,n(PDD)∶n(对苯二酚)=1∶1,收率为79%。
2.
) first in the absence of organic solvent, and then an oligomer polymeric pentaerythrityl phosphate was synthesized in yield 79% from PDD and hydroquinone (lequiv.
以季戊四醇、三氯氧磷为原料,采用无溶剂法首先合成了季戊四醇二磷酸酯二磷酰氯(PDD),n(季戊四醇):n(三氯氧磷)=1:5,收率为84％;然后以PDD和对苯二酚为原料,乙腈为溶剂,三乙胺为缚酸剂,在氮气氛围下合成了低聚阻燃剂聚季戊四醇磷酸酯,n(PDD):n(对苯二酚)=1:1,收率为79％。
5) melamine salt of pentaerythritol phosphate
季戊四醇磷酸酯蜜胺盐
1.
And in order to reduce the emission of pollutant,the intumescent flame retardant named melamine salt of pentaerythritol phosphate(MPP) was synthesized from phosphoric acid instead of phosphorus oxychloride(POCl_3) in the conventional technology.
(1)利用溶剂法制备了三聚氰胺磷酸盐(MP)、三聚氰胺焦磷酸盐(MPY)和三聚氰胺聚磷酸盐(MPOP),并用磷酸为原料代替传统的三氯氧磷制备了季戊四醇磷酸酯蜜胺盐(MPP),减少了污染物的排放,并通过对中间体-季戊四醇磷酸酯的制备及表征,推测出季戊四醇磷酸酯蜜胺盐(MPP)的结构及反应机理;(2)利用新颖的固相化学法制备了三聚氰胺聚磷酸盐(MPOP)和季戊四醇磷酸酯蜜胺盐(MPP),制备过程环保无污染;(3)本文考察了反应温度、反应时间及其原料比等条件对反应的影响,并通过单因素及正交实验得出溶剂法和固相化学法的较佳合成工艺;利用FT-IR、MS、NMR、TG、DSC等方法对产物的结构、热性能进行表征与测试,结果表明产物红外光谱图与文献基本一致,同时初步探究了其反应机理和阻燃机理。
6) PEPA
笼状季戊四醇磷酸酯
1.
The intumescent flame retardant(IFR) PP was prepared by using Melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy1-2,6,7-trioxa-1-phosphabicyclooctane(PEPA) as flame retardants and Cr2O3 as synergistic agent.
以Cr2O3为阻燃协效剂,采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
2.
Halogen-free flame retardant polypropylene(PP) was prepared by using melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy 1-2,6,7-trioxa-1-phospha-bicyclooctane(PEPA) as flame retardants.
采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
3.
Intumescent flame retardant(IFR) polypropylene(PP) was prepared by using Melamine polyphosphate(MPP) and 1-oxo-4-hydroxymethy1-2,6,7-trioxa-1-phospha-bicyclo-octane(PEPA) as flame retardants and 4A Zeolite as synergistic agent.
以4A分子筛为阻燃协效剂,采用多聚磷酸蜜胺(MPP)和笼状季戊四醇磷酸酯(PEPA)复配阻燃剂,制备了具有良好阻燃性能的无卤阻燃PP。
补充资料：二亚磷酸季戊四醇二硬脂醇酯
分子式：C41H82O6P2
分子量：733.06
CAS号：3806-34-6
性质：白色蜡状固体。熔点54-56℃，相对密度0.940-0.960（50/15.5℃），折光率1.4610-1.4660（50℃）。溶解度（g/100g溶剂，25℃）：苯14.7，已烷0.3，氯仿45.0，丙酮0.3，甲醇0.3；不溶于水。
制备方法：由二氯代季戊四醇二亚磷酸酯与十八碳醇反应而得。其中二氯代季戊四醇二严磷酸酯是由季戊四醇与三氯化磷反应得到。另一种生产方法是以季戊四醇和亚磷酸三苯酯反应，再与十八碳醇进行酯交换得到该品。
用途：该品为辅助抗氧剂，适用于聚乙烯、聚丙烯、聚氯乙烯和聚酯等。制品透明性好，不污染，与紫外线吸收往日战斗英雄用有协同效应。
分子量：733.06
CAS号：3806-34-6
性质：白色蜡状固体。熔点54-56℃，相对密度0.940-0.960（50/15.5℃），折光率1.4610-1.4660（50℃）。溶解度（g/100g溶剂，25℃）：苯14.7，已烷0.3，氯仿45.0，丙酮0.3，甲醇0.3；不溶于水。
制备方法：由二氯代季戊四醇二亚磷酸酯与十八碳醇反应而得。其中二氯代季戊四醇二严磷酸酯是由季戊四醇与三氯化磷反应得到。另一种生产方法是以季戊四醇和亚磷酸三苯酯反应，再与十八碳醇进行酯交换得到该品。
用途：该品为辅助抗氧剂，适用于聚乙烯、聚丙烯、聚氯乙烯和聚酯等。制品透明性好，不污染，与紫外线吸收往日战斗英雄用有协同效应。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。