1) anti-welding characteristic
抗熔焊特性
1.
The main problem of the anti-welding characteristic of AgRENi electrical contact material was investigated on special DC condition.
研究了AgRENi电接触材料特定直流条件下的抗熔焊特性以及电弧对AgRENi电接触材料微观形貌及元素分布的影响。
2) melting-welding resistance
抗熔焊性
1.
It is found that compound materials with proper Fe3Al process well electric conductivity,excellent oxidation resistance,melting-welding resistance and mechanics.
结果表明,添加适量Fe3Al可使复合材料具有较高的电导率、优良的抗氧化性和抗熔焊性以及良好的力学性能,能够取代Ag基电接触复合材料,达到节Ag的目的。
3) melting characteristic (of an electrode)
熔化特性(焊)
4) welding resistance
抗熔焊
1.
This paper introduced the types of surface deterioration of electrical contact materials and finished the experiments of welding resistance for AgCdO,AgSnO 2,AgNi and their different pairings,analysed the changes of surface composition and distribution as well as the relationship between component distribution and the thermal parameter θ mC pρmλ .
阐述了电触头材料表面劣化的分类，对ＡｇＮｉ，ＡｇＣ－ｄＯ，ＡｇＳｎＯ２及其不同配对时的抗熔焊性能进行了对比实验；分析了交流电弧作用下材料成分含量分布变化规律与金属θｍＣｐρｍλ间的关系。
5) antidripping
抗熔滴性
1.
The results indicate that a small amount of PA5935 dosaged into PET improved its antidripping and charring properties,but its oxygen index and tensile strength decreased.
将聚对苯二甲酸乙二醇酯(PET)与PA5935高速共混,注射制样,样品的热性能、力学性能、阻燃性能和流变性能等测试结果表明,在PET中加入少量PA5935改善了PET抗熔滴性能与炭化性能,但结晶度、氧指数和部分力学性能下降。
6) freeze-thaw resistance
抗冻熔性
补充资料：熔焊稀释率
熔焊稀释率
rate of dilution
ronghan xlshlld熔焊稀释率(rate of dilution)金属熔焊或堆焊时，熔教金属被稀释的程度，用母材或预先堆焊层金属在焊缝金属中所占的百分比(即熔合比)来表示。通常，填充金属的成分同母材成分往往并不相同，特别‘是异质金属相焊或合金堆焊时。当堆焊金属的合金成分主要来自填充金属时，局部熔化了的母材在焊缝中的效果可以认为是稀释。因此，熔合比又常称为稀释率。在所有电弧焊焊缝中，都有一定数量的熔化母材和填充金属相混合，只有少数焊缝金属成分与母材成分一样，且因焊缝组织的性质有些独特，所以母材被焊缝过多的稀释而引起成分变化，就会影响焊缝金属的性能，从而影响金属焊接性。 (李维茜)