1) 3,3-Bis(bromomethyl) oxetane
3,3-双溴甲基氧丁环
1.
3,3-Bis(bromomethyl) oxetane(BBMO) was synthesized from tribromoneopentyl alcohol(TBNPA) in the presence of alkali via homogeneous reaction with ethanol as solvent or phase transfer reaction with tetrabutylammonium bromide as phase transfer catalyst.
以三溴新戊醇(TBNPA)为原料,在碱作用下,分别采用以乙醇作溶剂的均相法和以溴化四丁基铵作相转移催化剂的两相法(甲苯/水)合成了3,3-双溴甲基氧丁环(BBMO)。
2) 3,3-dibromomethyl oxetane
3,3-双溴甲基氧杂环丁烷
1.
Using water and toluene as solvent,quaternary ammonium salt as phase transfer catalyst,under the effect of NaOH,3,3-dibromomethyl oxetane(BBMO) was synthesized by the cylization of 1,1,1-tribromomethyl-1-hydroxymethyl methane.
以1,1,1-三溴甲基-1-羟甲基甲烷为原料、水和甲苯为反应溶剂、季铵盐为相转移催化剂,在NaOH的作用下经关环反应合成3,3-双溴甲基氧杂环丁烷(BBMO);以季铵盐为相转移催化剂,BBMO在水相介质中经叠氮基取代反应制备出3,3-双叠氮甲基氧杂环丁烷(BAMO);用红外、核磁表征产品结构,高效液相色谱分析产品纯度。
3) poly[3,3-bis (bromomethyl)trimethylene oxide]thermoelectric film
聚[3,3-双(溴甲基)氧杂环丁烷]热电薄膜
4) poly[3,3-bis(bromomethyl)trimethylene oxide]
聚[3,3-双(溴甲基)氧杂环丁烷]
5) Pentone
['pentəun]
聚3,3-双(氯甲基)丁氧环
6) polychloroether
聚3,3-双(氯甲基)丁氧环
补充资料：聚3,3-双(氯甲基)丁氧环
分子式：
CAS号：
性质：又称聚3,3-双(氯甲基)丁氧环，聚氯醚，片通(Pentone)。分子链的重复结构单元为的聚合物。稍带微黄的乳白色结晶。相对密度1.4。熔融温度178～187℃。脆化温度-40℃。热分解温度290℃。热变形温度(1.82MPa)99℃。可在-30～十120℃长期使用。化学稳定性仅次于聚四氟乙烯(PTFE)。耐候性、阻燃性和电性能优良。拉伸强度(MPa)43.12～54.88，弯曲强度(MPa)72～78，压缩强度(MPa)62～74，悬臂梁冲击强度(缺口)1.57～2.16kJ/m2。体积电阻率>1.0×1016Ω·cm，介电常数(60Hz)3.1～3.3。由3,3-双(氯甲基)丁氧环开环聚合制得。可用多种方法加工成不同制品。可用作机械、仪表、电器、医疗器械的零部件，化工、石油、冶金、矿山用防腐材料。
CAS号：
性质：又称聚3,3-双(氯甲基)丁氧环，聚氯醚，片通(Pentone)。分子链的重复结构单元为的聚合物。稍带微黄的乳白色结晶。相对密度1.4。熔融温度178～187℃。脆化温度-40℃。热分解温度290℃。热变形温度(1.82MPa)99℃。可在-30～十120℃长期使用。化学稳定性仅次于聚四氟乙烯(PTFE)。耐候性、阻燃性和电性能优良。拉伸强度(MPa)43.12～54.88，弯曲强度(MPa)72～78，压缩强度(MPa)62～74，悬臂梁冲击强度(缺口)1.57～2.16kJ/m2。体积电阻率>1.0×1016Ω·cm，介电常数(60Hz)3.1～3.3。由3,3-双(氯甲基)丁氧环开环聚合制得。可用多种方法加工成不同制品。可用作机械、仪表、电器、医疗器械的零部件，化工、石油、冶金、矿山用防腐材料。