1) SBA-16 thin film
SBA-16膜
1.
The mesoporous SBA-16 thin films were synthesized with ITO as the substrate under acidic condition.
7V,沉积时间为50min,在SBA-16膜/ITO电极表面电沉积生长出"花状"CdS纳米晶体,利用SEM、TEM等技术研究了CdS纳米晶体形貌和结构,同时进行了荧光光谱测试。
2) modified SBA-16 film
改性SBA-16薄膜
3) Ru-PPh_2-SBA-16
Ru-PPh2-SBA-16
1.
The PPh_2-SBA-16 was used as a support to immobilize the Ru(Ⅱ) ions through strong coordination between PPh_2-group and Ru(Ⅱ), denoted as Ru-PPh_2-SBA-16.
以2-(二苯基膦)乙基三乙氧基硅烷和正硅酸乙酯为混合硅源,采用延时共缩聚法经表面活性剂F127自组装合成了二苯基膦(PPh2)修饰的SBA-16纳米介孔分子筛(PPh2-SBA-16),通过PPh2配体络合Ru(Ⅱ)化合物制备出固载化的Ru(Ⅱ)非均相催化剂(Ru-PPh2-SBA-16),样品仍然保持了SBA-16的规整孔道结构。
5) Fe 16 N 2 thin fi
Fe_(16)N_2薄膜
6) mesoporous SBA-15
介孔SBA-15
1.
Siliceous mesoporous SBA-15 has been proposed as a new effective structural promoter to pre- pare highly effective SiO2-modified Cu/ZnO/Al2O3 catalysts for hydrogen production.
以介孔SBA-15为结构助剂,制备出用于甲醇水蒸气重整制氢的新型高效氧化硅掺杂的Cu/ZnO/Al2O3催化剂,并与传统Cu/ZnO/Al2O3催化剂在相同条件下的催化性能进行了比较。
2.
Mesoporous SBA-15 was prepared by using Pluronic P123 triblock copolymer as struc-ture-directing agents and Au-modified mesoporous SBA-15 (Au-SBA-15) was synthesized by a Deposi-tion-Precipitation methods.
以P123嵌段共聚物表面活性剂为模板剂制备介孔氧化硅SBA-15,并用沉积-沉淀(DP)法在SBA-15介孔表面负载纳米Au颗粒制备得到金复合介孔SBA-15材料(Au-SBA-15)。
补充资料：电解食盐水溶液离子膜电解槽所用的膜材料之一
分子式：
CAS号：
性质：又称全氟羧酸-磺酸复合离子膜 Rf-COOH-Rf-SO3H 电解食盐水溶液离子膜电解槽所用的膜材料之一。使用时，将较薄的羧酸层面向阴极，较厚的磺酸层面向阳极，因而兼有羧酸膜和磺酸膜的优点。由于Rf-COOH层的存在，可阻挡氢氧离子返迁移到阳极室，确保了高的电流效率（96%），因Rf-SO3层的电阻低，能在高电流密度下运行，且阴极液可用盐酸中和，产品氯气中氧含量低，氢氧化钠浓度可达33%～35%。可在全氟磺酸膜上涂敷一层全氟羧酸的聚合物，或是将磺酸膜和羧酸膜进行层压，或是采用化学方法处理而制得的复合膜。现以采用化学方法处理者质量最佳。
CAS号：
性质：又称全氟羧酸-磺酸复合离子膜 Rf-COOH-Rf-SO3H 电解食盐水溶液离子膜电解槽所用的膜材料之一。使用时，将较薄的羧酸层面向阴极，较厚的磺酸层面向阳极，因而兼有羧酸膜和磺酸膜的优点。由于Rf-COOH层的存在，可阻挡氢氧离子返迁移到阳极室，确保了高的电流效率（96%），因Rf-SO3层的电阻低，能在高电流密度下运行，且阴极液可用盐酸中和，产品氯气中氧含量低，氢氧化钠浓度可达33%～35%。可在全氟磺酸膜上涂敷一层全氟羧酸的聚合物，或是将磺酸膜和羧酸膜进行层压，或是采用化学方法处理而制得的复合膜。现以采用化学方法处理者质量最佳。