1) branched glycidyl azide polymer nitrate(B-GAPN)
支化聚叠氮缩水甘油醚硝酸酯(B-GAPN)
2) branched glycidyl azide polymer (B GAP)
支化叠氮缩水甘油醚聚合物(B-GAP)
3) branched glycidyl azide polymer(B-GAP)
支化聚叠氮缩水甘油醚(B-GAP)
4) PGN
聚缩水甘油醚硝酸酯
1.
This paper investigated the synthesis methods of the three energetic binders poly(glycidyl nitrate)(PGN),poly(3,3-bis(azidomethyl) oxetane)(PBAMO) and glycidyl azide-r-bis(azidomethyl)oxetane copolymer(BAMO-GAP).
本论文研究了聚缩水甘油醚硝酸酯(PGN)、聚双叠氮甲基氧杂环丁烷(PBAMO)和双叠氮甲基氧丁环-叠氮缩水甘油醚共聚物(BAMO-GAP)三种新型含能粘结剂的合成方法。
5) glycidyl azide polymer
聚叠氮缩水甘油醚
1.
Synthetic methods, synthetic routes and new advances of glycidyl azide polymer(GAP) plasticizers are outlined.
概述聚叠氮缩水甘油醚(GAP)增塑剂的合成方法、合成路线及新进展,重点介绍了端羟基GAP、端叠氮基GAP、端酯基GAP和端酯基端叠氮基GAP增塑剂的合成。
2.
Branched glycidyl azide polymer(B GAP) was prepared from industrial polyepichlorohydrin(PECH) rubber as a starting material after reaction with sodium azide.
以工业氯醇橡胶为原料 ,通过与叠氮化钠反应制备出支化聚叠氮缩水甘油醚 (B GAP)。
6) glycidyl nitrate(GN)
缩水甘油醚硝酸酯(GN)
1.
The synthetic route of glycidyl nitrate(GN) was improved.
为了改进缩水甘油醚硝酸酯(GN)的合成路线,以丙烯醇为原料,经间氯过苯甲酸环氧化后得到缩水甘油醇(GA),然后GA经硝酸/醋酐硝化后得到了GN,硝化产物GN的收率为70。
补充资料：缩水甘油基叠氮化物聚合物
分子式：
CAS号：
性质：常温下为琥珀色黏液。Mn1000-4000。△Hf+957kJ/kg。密度1.30g/cm3。Tg-45℃。起始分解温度224℃。冲击感度19.5J。常用的合成方法是用相应分子量的聚环氧氯丙烷进行叠氮化反应而制得。支化GAP的官能度7～11，Mn500～50 000。与相同分子量的线型GAP相比，其Tg低、黏度低、生成热高。它是用Mn约106的聚环氧氯丙烷与环氧氯丙烷、NaN3反应制得。GAP主要用作固体推进剂、枪炮发射药和不敏感高能炸药的黏合剂。
CAS号：
性质：常温下为琥珀色黏液。Mn1000-4000。△Hf+957kJ/kg。密度1.30g/cm3。Tg-45℃。起始分解温度224℃。冲击感度19.5J。常用的合成方法是用相应分子量的聚环氧氯丙烷进行叠氮化反应而制得。支化GAP的官能度7～11，Mn500～50 000。与相同分子量的线型GAP相比，其Tg低、黏度低、生成热高。它是用Mn约106的聚环氧氯丙烷与环氧氯丙烷、NaN3反应制得。GAP主要用作固体推进剂、枪炮发射药和不敏感高能炸药的黏合剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。