1) transformation from pearlite to austenite
珠光体转变奥氏体
2) austenlite/pearlite transformation
奥氏体珠光体相变
3) pearlite to austenite
珠光体→奥氏体
5) pearlite transformation
珠光体转变
1.
The critical cooling rate without pearlite transformation increases from 0.
结果表明:试验用钢只发生珠光体转变和马氏体转变;热变形明显地促进珠光体、马氏体转变;不发生珠光体转变的临界冷却速度由0。
2.
The critical cooling rate that does not occur pearlite transformation is 3.
不发生珠光体转变的临界冷却速度为３１℃／ｓ，Ｍｓ点为１５０℃。
6) reverted austenite
逆转变奥氏体
1.
The results show that the mixed microstructure of lath-like secondary tempered martensite + ferrite are obtained and a small amount of reverted austenite precipitate along the boundaries and inner of martensite in QLT-treated steel.
结果表明,10Ni5CrMo钢经两相区淬火处理后,得到板条状的二次回火马氏体+铁素体的混合组织,并且在板条边界及板条内部析出逆转变奥氏体,该逆转变奥氏体与基体遵从K-S关系。
2.
The austenite in the steel after aging is mainly reverted austenite.
结果表明,Custom 465钢的最佳固溶温度在900~950℃温度范围内;时效态钢中奥氏体主要为逆转变奥氏体。
3.
The content of reverted austenite in laser hardened sampl.
2;在同样的激光处理工艺条件下,经激光相变硬化后原始状态为淬火态试样的淬硬层的硬度和深度比退火态试样的要高和深;相变硬化后,随着回火时间的延长,逆转变奥氏体含量增多,硬化层硬度降低。
补充资料：奥氏体-贝氏体球铁
分子式：
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。