1) barium-bearing sulfoaluminate cement
硫铝酸钡钙水泥
2) alite-barium calcium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The effects of the composition of clinker minerals,gypsum content and environment temperature on the slurry rheological and dry shrinkage properties of alite-barium calcium sulphoaluminate cement were studied.
结果表明:阿利特—硫铝酸钡钙水泥的新拌浆体属于Bingham型流体,水泥浆体的屈服应力和黏度受熟料中硫铝酸钡钙矿物含量变化的影响较大,随石膏掺量的增加和环境温度的增高而减小;阿利特-硫铝酸钡钙水泥具有一定的微膨胀性能,其砂浆的干缩性能优于硅酸盐水泥砂浆。
2.
Experimental results show that when the slag content is 10% the compressive strength of alite-barium calcium sulphoaluminate cement reachs 44.
研究矿渣掺量对阿利特-硫铝酸钡钙水泥性能的影响,当质量分数掺量为10%时,阿利特-硫铝酸钡钙水泥3 d、28 d的强度分别达到44。
3.
The drying shrinkage and mechanical property of alite-barium calcium sulphoaluminate cement (SABC) mortars were investigated by contrasting with Portland cement mortars.
通过与硅酸盐水泥(portland cement,PC)对比,研究了阿利特-硫铝酸钡钙水泥(alite-barium calcium sulphoaluminate cement,SABC)砂浆的力学性能和干缩性能。
3) alite-calcium barium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The influence of different contents of slag,fly ash and zeolite powers on the strength of alite-calcium barium sulphoaluminate cement mortar is investigated,and the reaction mechanism is discussed.
研究不同掺量的矿渣、粉煤灰和沸石粉对阿利特-硫铝酸钡钙水泥砂浆强度的影响规律,并对其反应机理进行探讨。
2.
Effects of slag on the structure and properties of cement pastes were studied by determining the setting time, the mechanical property and pore structure of hardened Alite-Calcium Barium Sulphoaluminate cement pastes, and using scanning electron microscopy and DTA-TG.
通过对水泥浆体凝结性能、力学性能和孔结构的测定,结合扫描电镜分析和差热-热重分析,研究了矿渣掺量对阿利特-硫铝酸钡钙水泥浆体硬化浆体结构和性能的影响。
4) Alite-C2.75B1.25A3S cement
阿利特-硫铝酸钡钙水泥
1.
Compared with Portland cement concrete,the impermeability of Alite-C2.
在与相同配合比的普通硅酸盐水泥混凝土的对比试验中,采用抗渗试验和孔结构分析的方法,研究了阿利特-硫铝酸钡钙水泥混凝土的抗渗性能与水灰比的关系。
5) sulphoaluminate
硫铝酸钙
1.
Formation kinetics of high-temperature phase sulphoaluminate;
高温固硫物相硫铝酸钙生成动力学
2.
Study of sulfur-fixing characteristics of sulphoaluminate in different atmosphere at high temperature;
高温固硫物相硫铝酸钙在不同气氛下的固硫研究
3.
Study of high temperature phase of sulphoaluminate for desulfuration;
高温稳定物相硫铝酸钙固硫研究
6) calcium sulphoaluminate
硫铝酸钙
1.
Study on properties of Portland cement modified with calcium sulphoaluminate;
硫铝酸钙改性硅酸盐水泥性能研究
2.
Testing methods such as chemical analysis, X-ray diffraction and differential scanning calorimetry were used to study the influence of Fe2O3 on the formation of anhydrous calcium sulphoaluminate ( C 4 A 3S ).
借助化学分析方法、X射线衍射、差示扫描量热法等测试手段研究了Fe2O3对无水硫铝酸钙矿物(C4A3S)形成过程的影响。
3.
The kinds,shapes and quantities of hydration products and the ion concentration in pore solution were investigated during hydration of fly ash or slag portland cement containing calcium sulphoaluminate by differential scanning calorimetry-thermogravimetry analysis,scanning electron microscope and chemical analysis.
用差示扫描热重分析扫描电镜和化学分析法研究了含硫铝酸钙粉煤灰硅酸盐水泥和含硫铝酸钙矿渣硅酸盐水泥水化过程中水化产物的种类、形状、数量和孔溶液离子浓度等方面的变化规律。
参考词条
补充资料：硫铝酸盐水泥和铁铝酸盐水泥
硫铝酸盐水泥和铁铝酸盐水泥
sulPhoaluminateCement and ferralUminate eement
硫铝酸盐水泥和铁铝酸盐水泥Sulphoaluminatecement and ferraluminate eement以石灰石、矾土(SAC为铝矾土，FAC为铁钒土)和石膏为原料制成的水泥。原料在回转窑中低温缎烧成以C4A3S、CZS和C6AF:(或C;AF)为主要矿物组成的熟料，通过掺入适量掺合料并共同粉磨而成水泥。为区别于硅酸盐水泥(第一系列)、铝酸盐水泥(第二系列)而将其称为第三系列水泥。 硫铝酸盐(S AC)水泥和铁铝酸盐(F AC)水泥由中国研制成功，并分别于1974年和1983年投入工业生产。目前生产的SAC类水泥品种有快硬、高强、膨胀、自应力和低碱硫铝酸盐水泥(GRC专用水泥);FAC类水泥品种有快硬、高强、膨胀和自应力铁铝酸盐水泥。 硫铝酸盐水泥和铁铝酸盐水泥具有以下特性:①较高的早期强度，而且具有不断增长的后期强度和满足使用要求的凝结时间，12小时至1天的抗压强度可达35一60 MPa，抗折强度达6.5一7.SMPa;其高强水泥3天抗压强度可达80一100 MPa，抗折强度达9.0一11.OMPa。②膨胀性能可在很大范围内调节。根据实际应用需要，其砂浆自由膨胀可在0.05一1.5%之间调节，其自应力值可在0.5一5.OMPa之间调节。③在0一10oC低温下使用，其早期强度(1一3天)是同标号硅酸盐水泥混凝土的5一10倍。在0一一20aC低温下使用，加入少量外加剂，3一7天的混凝土强度可达设计标号的70一80%。在正、负温交替条件下施工，对后期强度增长影响不大。实验室300次冻融循环，混凝土强度损失不明显。④水泥石结构较致密，其混凝土抗掺性是同标号硅酸盐水泥混凝土的2一3倍。⑤对海水、氯盐(NaCI，MgC12)、硫酸盐(NaZSO‘、MgSO‘、(NH‘)250小尤其是它们的复合盐类(MgSO‘+NaCI)，均具有很好的抗腐蚀性。其中铁铝酸盐水泥类更优于硫铝酸盐水泥类。⑥硫铝酸盐水泥类混凝土因早期(前3天)水化液相碱度较低，钢筋有轻微锈蚀。随时间的推移，水泥水化液相碱度提高，水泥石微结构致密，因此后期锈蚀情况无发展。而铁铝酸盐水泥由于水化液相碱度较高，对钢筋无锈蚀。 第三系列水泥适用于各种建筑工程，预应力混凝土构件和水泥制品。特别适用于地下工程、海港工程、抢修和抢建工程，制作自应力水泥压力管，高强管、桩和各种GRC制品。(苏慕珍)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。