1) cold rolled Mg-9Li-1Zn alloy
冷轧Mg-9Li-1Zn合金
2) Mg-3Al-1Zn alloy
Mg-3Al-1Zn合金
1.
In this paper the effects of Sr on the as-cast microstructure of Mg-3Al-1Zn alloy are investigated,and the results indicate that there are no obvious effects of adding 0.
结果表明:在Mg-3Al-1Zn合金中加入0。
2.
In this paper the effects of Y on the as-cast microstructure of Mg-3Al-1Zn alloy were investigated,and results indicated that the effects of 0.
结果表明,在Mg-3Al-1Zn合金中加入w(Y)=0。
3.
3%Y to Mg-3Al-1Zn alloy can refine the grains of the alloy, and adding Sr can obtain higher efficiency than adding Y.
Sr和Y以及不同Sr加入量对Mg-3Al-1Zn合金晶粒的细化效果差异与不同条件下Mg-3Al-1Zn合金的开始结晶温度不同有关。
3) Mg-12Gd-4Y-1Zn-0.5Zr
Mg-12Gd-4Y-1Zn-0.5Zr合金
1.
Microstructures and Mechanical Properties of Mg-12Gd-4Y-1Zn-0.5Zr Alloy;
Mg-12Gd-4Y-1Zn-0.5Zr合金的显微组织和力学性能
4) Mg-6A1-1Zn-0.7Si alloy
Mg-6A1-1Zn-0.7Si合金
5) Mg-6Al-1Zn-Y alloy
Mg-6Al-1Zn-Y合金
6) cold rolled Al-Zr alloy
冷轧AI-Zr合金
补充资料：Li-Zn rectangular loop ferrite
分子式：
CAS号：
性质：以锂、锌、铁的氧化物为主要成分的尖晶石型铁氧体。化学式为(Li2O、ZnO)·Fe2O3。密度4.8g/m3左右。开关系数0.7μs·Oe。电阻率102Ω·cm。矫顽力Hc250～450A/m(2.5～4.5)矩形度Rr0.82～0.92。居里温度Tc300～400℃。配料(mol％)Li2O10～20，ZnO 3.5～20，Fe2O370～85。采用一般电子陶瓷工艺，在氧气或氮气气氛中烧结，可用于制造记忆磁芯。
CAS号：
性质：以锂、锌、铁的氧化物为主要成分的尖晶石型铁氧体。化学式为(Li2O、ZnO)·Fe2O3。密度4.8g/m3左右。开关系数0.7μs·Oe。电阻率102Ω·cm。矫顽力Hc250～450A/m(2.5～4.5)矩形度Rr0.82～0.92。居里温度Tc300～400℃。配料(mol％)Li2O10～20，ZnO 3.5～20，Fe2O370～85。采用一般电子陶瓷工艺，在氧气或氮气气氛中烧结，可用于制造记忆磁芯。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条