1) resistance to sulfate attack
抗硫酸盐侵蚀性能
1.
The resistance to sulfate attack,impermeability and mechanical performance are studied in the paper.
当聚灰比由0%提高到15%时,水泥试样的渗透高度下降了70%;随着苯丙乳液掺入量的增加,聚合物硫铝酸盐水泥的抗侵蚀系数增大,其抗硫酸盐侵蚀性能逐渐增强;苯丙乳液聚合物对硫铝酸盐水泥的抗折强度影响不大,当聚灰比小于15%时,聚合物硫铝酸盐水泥在28d龄期的抗折强度均在7。
2.
SEM,pore structure and resistance to sulfate attack were also studied.
采用SEM-EDS,孔结构分析和抗硫酸盐侵蚀性能测试等手段,研究了引发剂用量、聚灰比对聚合物硫铝酸盐水泥耐久性的影响。
3.
The cement with high volume of slag was made by chemical activation,then its resistance to sulfate attack was evaluated.
对通过化学激发自制的大掺量矿渣水泥的抗硫酸盐侵蚀性能进行评定:首先采用长期浸泡方法进行测定,评判指标为线膨胀率和抗折强度比,结果表明该矿渣水泥具有优异的抵抗高浓度硫酸盐侵蚀的性能;其次采用GB/T 749—2001规定的快速试验方法进行测定,测定结果与长期浸泡方法有异。
2) sulfate resistance
抗硫酸盐侵蚀性
1.
To systematically study the effects of mineral admixtures such as slag,expanding agent on sulfate resistance of concrete, a series of concrete immersion test was carried out.
通过混凝土的抗硫酸盐浸泡试验,系统研究了矿渣、膨胀剂等矿物掺合料对混凝土抗硫酸盐侵蚀性能的影响。
2.
The paper presents the favourable influence and improvement actions of slag on sulfate resistance of concrete.
从几个方面阐述了矿渣对混凝土抗硫酸盐侵蚀性能的改善作用,讨论了在矿渣使用过程中需要特别注意的掺加量和养护制度问题。
3) sulphate resistance
抗硫酸盐侵蚀
1.
Validity study on sulphate resistance to concrete by sodium citrate;
柠檬酸钠对混凝土抗硫酸盐侵蚀的有效性研究
2.
The results showed that the sulphate resistance of three companion specimens was the same, but the resistance of finely-broken stone concrete test prism to sulphate attack was most obvious.
系统地比较了三种强度等级的棱柱体砂浆、棱柱体细石混凝土和立方体混凝土的抗硫酸盐侵蚀破坏性能,结果表明三种试验试样的抗硫酸盐侵蚀性能基本相同,但相对而言棱柱体细石混凝土对于硫酸盐侵蚀破坏最为敏感。
4) sulfate resistance
抗硫酸盐侵蚀
1.
Comments on test methods for measuring sulfate resistance of concrete;
混凝土抗硫酸盐侵蚀性能的测试与评价方法综述
2.
The influence of water binder ratio and slag content on the ability of sulfate resistance of mortar is studied by experiments, and then the influence of slag addition on the ability of concrete is investigated.
通过实验研究了水胶比和矿渣微粉掺量对砂浆抗硫酸盐侵蚀能力的影响 ,并进一步研究了掺加矿渣微粉对混凝土抗硫酸盐侵蚀能力的影响 。
5) sulphate resisance agent
抗硫酸盐侵蚀剂
6) sulfate attack resistance
抗硫酸盐侵蚀
1.
Influence of interface structure on sulfate attack resistance of mortar with low W/C ratio;
界面结构对低水胶比高性能水泥砂浆抗硫酸盐侵蚀性能的影响
补充资料:抗硫酸盐硅酸盐水泥
分子式:
分子量:
CAS号:
性质:简称抗硫酸盐水泥。是以适当成分的生料,燃至部分熔融,所得的以硅酸钙为主的特定矿物组成的熟料,加入适量石膏,磨细制成的具有一定抗硫酸盐侵蚀性能的水硬性胶凝材料。该水泥按强度等级分为325、425和525三个标号。适用于一般受硫酸盐侵蚀的海港、水利、地下、隧涵、引水、道路和桥梁基础等工程。抗硫酸盐水泥一般可抵抗硫酸根离子浓度不超过2500毫克/升的纯硫酸盐的腐蚀。
分子量:
CAS号:
性质:简称抗硫酸盐水泥。是以适当成分的生料,燃至部分熔融,所得的以硅酸钙为主的特定矿物组成的熟料,加入适量石膏,磨细制成的具有一定抗硫酸盐侵蚀性能的水硬性胶凝材料。该水泥按强度等级分为325、425和525三个标号。适用于一般受硫酸盐侵蚀的海港、水利、地下、隧涵、引水、道路和桥梁基础等工程。抗硫酸盐水泥一般可抵抗硫酸根离子浓度不超过2500毫克/升的纯硫酸盐的腐蚀。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条