1) poly[(methylsilylene)ethynylene]
聚甲基硅次乙炔基硅烷
1.
Study on the isothermal pretreatment of poly[(methylsilylene)ethynylene];
聚甲基硅次乙炔基硅烷等温预处理过程的研究
2) 1,2-ethynediylbis[trimethyl-silan
二(三甲基甲硅烷基)乙炔
3) trimethylsilylacetylene
乙炔基三甲基甲硅烷
4) Polytrimethylsilyl propyne
聚三甲基甲硅烷基丙炔
5) methyl-tri(phenylethynyl)silane
甲基三苯乙炔基硅烷
1.
Two high temperature resistant silicone resin,methyl-di(phenylethynyl)silane and methyl-tri(phenylethynyl)silane were synthesized by the reaction of phenylacetylide,methyldichlorosilane and methyltrichlorosilane in the presence of lithium.
以苯乙炔与甲基二氯硅烷、甲基三氯硅烷在有机锂试剂中反应,合成了甲基二苯乙炔基硅烷(MD-PES)和甲基三苯乙炔基硅烷(MTPES)2种新型耐高温有机硅树脂。
6) Methyl-di-phenylacetylene-silane
甲基二苯乙炔基硅烷
1.
Modification of PBI by Methyl-di-phenylacetylene-silane;
甲基二苯乙炔基硅烷改性聚苯并咪唑
2.
Polymer of methyl-di-phenylacetylene-silane(MDPES) possesses excellent properties of high temperature-resistance,low dielectric dissipation fraction,etc,but its mechanical property is not significant for its poor bonding with glass-fiber.
甲基二苯乙炔基硅烷(MDPES)聚合后具有耐高温、低介电损耗等优异性能,但力学性能低。
补充资料：聚甲基乙炔
分子式：
CAS号：
性质： 又称聚丙炔。是聚乙炔导电聚合物的同系物,外观呈现橘黄色。与聚乙炔相比其电导率下降，在非掺杂状态电导率约为10-11S/cm(非掺杂聚乙炔的电导率σ在10-5～10-9S/cm之间)，其原因可能是甲基的存在影响了双键之间的共平面作用。其化学稳定性也有所下降，因此作为导电材料其使用价值不大，在研究聚合反应和导电机理方面有一定意义。在一定分子量范围内聚合物的溶解度有所增加。其合成方法与聚乙炔类似，一般也可以用Ziegler催化剂催化反应制备，过渡金属络合物也是有效的催化剂。典型的合成反应过程如下：
CAS号：
性质： 又称聚丙炔。是聚乙炔导电聚合物的同系物,外观呈现橘黄色。与聚乙炔相比其电导率下降，在非掺杂状态电导率约为10-11S/cm(非掺杂聚乙炔的电导率σ在10-5～10-9S/cm之间)，其原因可能是甲基的存在影响了双键之间的共平面作用。其化学稳定性也有所下降，因此作为导电材料其使用价值不大，在研究聚合反应和导电机理方面有一定意义。在一定分子量范围内聚合物的溶解度有所增加。其合成方法与聚乙炔类似，一般也可以用Ziegler催化剂催化反应制备，过渡金属络合物也是有效的催化剂。典型的合成反应过程如下：
说明：补充资料仅用于学习参考，请勿用于其它任何用途。