1) short and long fatigue crack
长短疲劳裂纹
3) short fatigue crack
疲劳短裂纹
1.
Propagation behaviours of short fatigue cracks of titanium alloy-weld;
钛合金焊缝表面疲劳短裂纹的扩展行为
2.
Analysis of the Collective Evolution of High Temperature Low-cycle Short Fatigue Crack under Complex Stress Condition;
复杂应力状态下高温低周疲劳短裂纹群体演化行为研究
3.
The grouping behaviour of short fatigue cracks on surface of the weld metal for TC2 titanium alloy was investigated according to the replicating experiment, and the replicas were analyzed on the basis of fractal theory.
采用覆型技术,对TC2钛合金焊缝金属表面疲劳短裂纹群体演化行为进行了实验研究,并应用分形理论对实验观测结果进行了分析·结果表明,钛合金焊缝金属表面群体疲劳短裂纹演化行为具有分形特征;随着疲劳进程中循环次数的不断增加,分形维数也随之增大,对应着材料的损伤在不断加剧;分形维数可以作为一个损伤变量,更好地描述材料的疲劳损伤及演化
4) Short fatigue cracks
疲劳短裂纹
1.
Research on similarity of colony behavior between virus feature and short fatigue cracks;
病毒特征与疲劳短裂纹群体行为的相似性研究
2.
s:Two important methods applied in life sciences to describe damage fatigue of materials are discussed,including BP(back-propagation)neural network describing collective short fatigue cracks and input of transient energy healing fatigue damage of metal.
结合材料损伤和病毒学的相关研究成果 ,指出疲劳短裂纹和病毒在微观形态 ,生长环境 ,以及演化过程各阶段上具有相似性 ,提出基于病毒特征短疲劳裂纹群体行为统计相似性研究策略包括机理建模、裂纹遗传特征和材料免疫应答研究 。
3.
Low cycle short fatigue cracks at high temperature was experimentally studied with the material 16MnR under multiaxial stress.
模型考虑了材料细观组织、细观结构影响及裂纹之间的相互作用,并用该模型对16MnR材料表面疲劳短裂纹群体演化全过程进行了数值模拟分析,结果表明模拟结果与实验结果基本一致,该模型能有效地用于短裂纹的模拟。
6) long fatigue crack
疲劳长裂纹
1.
Probabilistic model of random-long fatigue crack propagation rates;
随机疲劳长裂纹扩展率的新概率模型
2.
Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel.
试验研究了随机疲劳长裂纹扩展率概率模型。
3.
A so_called "local probabilistic Paris relation method" was presented for measuring the random thresholds of long fatigue crack propagation.
提出了合理测定随机疲劳长裂纹扩展门槛值的"局部概率Paris关系法"· 揭示了常规法不能保证各试样门槛值数据处于相同扩展率水平,测定结果不尽合理的缺陷· 以Paris_Erdogan方程描述门槛值附近局部试验数据,考虑数据分散性规律和试样数量两方面的影响,在应力强度因子服从对数正态分布下建立了包含存活概率和置信度的局部概率关系模型,以可接受临界扩展率对应概率因子为依据测定概率门槛值· LZ50钢车轴试验数据分析验证了方法的合理性和有效性·
补充资料：疲劳裂纹生长
分子式：
CAS号：
性质：材料在连续交变应力作用下，会在其表面逐渐生成裂纹，并随着作用时间而逐渐向纵深发展，使裂纹扩展，试件的力学性能下降，最终导致完全断裂。应该指出，有些材料耐初始裂纹生长的性能很好，但一旦生成却发展很快。而另一些材料就正好相反。所以对疲劳裂纹的生成和发展是疲劳试验中最关心的性状之一。
CAS号：
性质：材料在连续交变应力作用下，会在其表面逐渐生成裂纹，并随着作用时间而逐渐向纵深发展，使裂纹扩展，试件的力学性能下降，最终导致完全断裂。应该指出，有些材料耐初始裂纹生长的性能很好，但一旦生成却发展很快。而另一些材料就正好相反。所以对疲劳裂纹的生成和发展是疲劳试验中最关心的性状之一。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条