1) rare earth complex coupling agent
稀土复合偶联剂
1.
Aluminum hydroxide was modified with rare earth complex coupling agent and the perfor- mance of the product was compared with those modified with other coupling agents including silane and titanate.
选用稀土复合偶联剂和有机硅烷、钛酸酯等常用偶联剂分别对氢氧化铝进行改性并比较其改性效果,结果表明,用稀土复合偶联剂改性氢氧化铝的效果最好,其活化指数由0上升至99%以上,吸油值从0。
2) rare-earth coupling agent
稀土偶联剂
1.
By way of the changes of mechanical properties of high molecular materials before and after weathering experiments, effects of rare-earth coupling agent(WOT) on weathering-resistant properties of PP/ CaCO3,PP/ Mg(OH)2,PP/ BaSO4 composites were studied.
通过高分子材料自然老化实验前后力学性能的变化,研究了稀土偶联剂WOT对PP／CaCO3、PP／Mg(OH)2、 PP／BaSO4复合体系的老化性能的影响。
2.
Wood powder was surface treaded with rare-earth coupling agent(WOT) and the modified wood powder was analyzed by infrared spectrum.
用稀土偶联剂(WOT)处理木粉,对改性木粉进行了红外光谱分析;将改性木粉、再生聚丙烯(PP)及其它助剂用双螺杆造粒机组挤出造粒制备PP/木粉复合材料,研究了WOT用量、木粉用量对复合材料性能的影响,并采用扫描电子显微镜进行了材料断面的形态分析。
3) Rare Earth Coupling Agent
稀土偶联剂
1.
Influences of Rare Earth Coupling Agent on Property of PP/Mica;
稀土偶联剂对PP/云母体系性能的影响
2.
The optimal conditions for rare earth coupling agent and Wt-200S as the compound modifiers for magnesium hydroxide as following:mass concentration fraction of sizing agent was 30%,mass ratio of rare earth coupling agent to Wt-200S was 1.
选择稀土偶联剂/螯合磷酸酯钛偶联剂作为氢氧化镁的复合改性剂,采用湿法改性处理氢氧化镁。
3.
The superficial modification of calcium carbonate using rare earth coupling agent,aluminate coupling agent,and stearic acid were carried out.
采用稀土偶联剂、铝酸酯和硬脂酸对CaCO3进行表面改性,测试其吸油值和黏度;表征了稀土偶联剂改性CaCO3抽提前后的红外光谱和扫描电镜;测定了稀土偶联剂改性CaCO3共混PP的抗冲击强度。
4) rare earth titanium coupling agent
稀土钛偶联剂
5) composite coupling agent
复合偶联剂
1.
A new interfacial reinforcing agent is introduced in the composite material of calcium carbonate/polyethylene,and it compounds with coupling agent to form a composite coupling agent,which can greatly reinforce the interfacial combination strength between calcium carbonate and polyethylene,and then greatly improve the impact strength of casting plastic products.
在碳酸钙-聚乙烯复合材料的界面之间,引入了一种新型的界面增强剂与偶联剂复合,大大提高了碳酸钙与聚烯烃的界面结合强度,从而大幅度提高注塑产品的冲击强度;考察了复合偶联剂的配比及其含量、碳酸钙的含量对复合材料性能的影响。
6) rare earth mixed inoculant
稀土复合孕育剂
1.
Investigates the effect of rare earth mixed inoculant RCC on the properties and structure of gray iron with low Cr Mo content.
研究了稀土复合孕育剂ＲＣＣ对高碳当量低铬钼灰铸铁性能和组织的影响。
补充资料：A-1160硅烷偶联剂
A-1160硅烷偶联剂化学名称为γ-脲基丙基三乙氧基硅烷(γ-Ureidopropyltriethoxysilane)，结构式为H2NCONHCH2CH2CH2Si(OC2H5)3，分子量264，无色液体，相对密度0.99，溶于水。
适用于环氧树脂、酚醛树脂、三聚氰胺甲醛树脂等胶粘剂。贮存于阴凉、干燥的库房内，防潮。
适用于环氧树脂、酚醛树脂、三聚氰胺甲醛树脂等胶粘剂。贮存于阴凉、干燥的库房内，防潮。