1) crystallization reaction
析晶(晶化)反应
2) reactive crystallization
反应析晶
1.
The results show that when the addition of fluormica was less than 20% (in mass fraction, the same below), diopside was formed via reactive crystallization; when 40% fluormica was added, fluoramphibole was formed.
用X射线衍射、扫描电镜研究了不同加入量氟云母晶体的钠钙玻璃粉末在烧结过程中的反应析晶。
2.
Heating up to 850 ℃,fluoramphibole is formed by a reactive crystallization between fluormica and glass,which had a significant influence on the densification.
加热至850℃,氟云母与玻璃发生反应析晶形成氟闪石,对致密化影响很大。
3) Solid StateReaction Amorphization
固态反应非晶化
4) solid state amorphization reaction
固态非晶化反应
1.
The solid state amorphization reactions induced by a constant-heating-rate annealing in themultilayers were studied by means of XRD,SEM,TEM,DSC and magnetic analysis.
使用 XRD,SEM,TEM,DSC 和磁性分析方法研究了该多层由恒速升温退火导致的固态非晶化反应。
5) crystallochemical reactivity
结晶化学反应性
6) peritectic reaction
包晶反应
1.
Delayed Phenomenon of Peritectic Reaction Under Non-equilibrium Cooling
非平衡凝固时包晶反应滞后现象的研究
2.
Through observation of SEM phase micrographs of specimen heat-treated at different conditions,the peritectic reaction μAl.
通过对名义成分为Al11Cr2的铸锭在不同温度下进行退火处理后的金相分析,首次观察到了包晶反应μ-Al4Cr+Lη-Al11Cr2,且证实了共析反应η-Al11Cr2-μAl4Cr+-θAl7Cr的存在。
3.
It is researched the influence of cooling rate and the content of silicon and manganese alloy on peritectic reaction and position of peritectic point in Fe-C alloy.
研究了冷却速率和硅、锰合金元素含量对Fe-C合金的包晶反应和包晶点位置的影响;由于CSP薄板坯冷却速率快,Fe-C相图向左下方移动,包晶反应区域的碳含量为0。
补充资料：加核晶析
分子式：
CAS号：
性质： 或称为加晶种的结晶，是一种结晶操作。在待结晶的溶液中加入一定量和一定粒度分布的溶质晶粒作为晶种或晶核，以促进溶质从溶液中结晶析出，并借以对结晶产品中粒度的分布进行控制。
CAS号：
性质： 或称为加晶种的结晶，是一种结晶操作。在待结晶的溶液中加入一定量和一定粒度分布的溶质晶粒作为晶种或晶核，以促进溶质从溶液中结晶析出，并借以对结晶产品中粒度的分布进行控制。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条