1) premelted dephosphorizer
预熔脱磷剂
1.
With CaO-Fe2O3-CaF2 system slag as dephosphorizer,the influencing factors of such premelted dephosphorizer,composition,addition rate,treating temperature,initial phosphors content in hot metal and granularity of premelted slag was studied in laboratory.
在实验室条件下,以CaO-Fe2O3-CaF2为预熔脱磷剂的主要渣系,对预熔脱磷剂的配比关系、加入量、处理温度、初始铁水磷含量以及预熔渣粒度进行了研究。
2) pre-melted desulfurizer
预熔脱硫剂
3) deoxidizing flux
脱氧熔剂
4) Degassing flux
脱气熔剂
5) dephosphorizing agent
脱磷剂
1.
The experiment principle and method of dephosphotrzation of high silicon ferromanganese silicon outside the SAF is described in this paper,the results show that using CaSi CaF 2 CaO as the dephosphorizing agent,the averrage dephosphorization rates are 31.
结果表明,使用CaSiCaF2CaO作脱磷剂,采用倒包法和喷吹法高硅锰硅合金的平均脱磷率分别为3154%和4132%。
2.
The precipitation dephosphorization on ferromanganese-silicon was studied in this work with calcium dephosphorizing agent and the slag of CaO-CaF_2.
选用钙系脱磷剂、CaO-CaF_2渣,对锰硅铁合金进行沉淀脱磷,着重研究脱磷剂加入量和锰硅铁合金中硅含量增量对脱磷效果的影响。
3.
Using pure iron,copper oxide,tin granular,tungsten particle and little vanadium pentexide served as flux,inspecting the sulfur content in dephosphorizing agent by the high frequency infrared carbon-sulfur detector.
以纯铁、氧化铜、锡粒、钨粒和少量的五氧化二钒为助熔剂,采用高频红外碳硫仪测定脱磷剂中的硫含量。
6) dephosphorization
[di:fɔsfərai'zeiʃən]
脱磷剂
1.
The results show that the absorbent removing phospholipids has some effect of declouring crude oil,and under the conditions of absorbent 3%,75℃ and duration 15 min,the best dephosphorization and decolouration results can be obtained.
实验主要采用物理吸附剂的方法脱去毛油中的磷脂,探讨了脱磷剂用量、温度、时间对脱磷效果的影响。
补充资料：熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
熔盐电解法生产铌粉(见熔盐电解法生产钽粉)
production of niobium powder by molten salt electrolysis
rongyand+onjlefa ShengChan n.fen熔盐电解法生产妮粉(produetion。fn;obi-um powder by molten salt eleetrolysls)见熔盐电解法生产担粉。