1) solid-state redox reaction
固相氧化反应
1.
In this paper,MnO2 nanorods were successfully synthesized firstly by solid-state redox reaction in the presence of a nonionic surfactant(PEG-400).
本文在前期利用低热固相氧化反应制备球状纳米MnO2电极材料研究[3]的基础上,首次借助表面活性剂辅助低热固相氧化反应成功地合成了MnO2纳米棒,并对其晶型和形貌大小进行了表征。
2) solid state redox reaction
固相氧化还原反应
1.
Nanoparticles of MnO2 were prepared by onestep solid state redox reaction at room temperature or 60 .
本文采用固相氧化还原反应体系直接合成出纳米α。
3) solid state reaction
固相化学反应
1.
Spinel type complex oxide nanocrystalline powders ZnFe 2O 4 was synthesized by solid state reaction at room temperature with inorganic reagent.
以无机盐为原料 ,采用室温固相化学反应法合成了尖晶石型复合氧化物ZnFe2 O4,X射线粉末衍射 (XRD)、透射电镜(TEM )等表征结果表明 ,固相反应完全 ,平均粒径约为 3 0nm左右 ;将样品制成烧结型气敏元件 ,发现在较低的工作温度时 ,对H2 S有较高的灵敏度和选择
2.
N-type semiconductoring nanometer oxides including SnO 2?In 2O 3?ZnO?Fe 2O 3 were prepared by solid state reaction of inorganic compound at room temperature.
以无机盐为原料 ,用室温固相化学反应直接合成了SnO2 、In2 O3 、ZnO、Fe2 O3 等半导体金属氧化物的纳米粉体 ,用X -射线衍射技术和透射电子显微镜对产物的物相和形貌进行了表征观察 ,结果表明 ,固相化学反应完全 ,所得产物为理论产物 ,且均为纳米粒
3.
The solid state reactions of Cu(OAc)2·H2O with 1 - phenyl - 3 - methyl - 4 -benzoylpyrazolone- 5(HPMBP,keto form and enol form) have been studied at low heating temperature( < 100℃).
在低加热条件下(<100℃),研究了Cu(OAc)_2·H_2O与1-苯基-3-甲基-4-苯甲酰基吡唑啉酮-5(HPMBP)两种异构体(烯醇式与酮式)的固相配位化学反应,结果表明两种异构体与Cu(OAc)_2·H_2O固相化学反应活性并不相同。
4) gas-solid catalytic reaction
气固相催化反应
1.
effect of inside-outside diffusion process on reaction selectivity in gas-solid catalytic reaction was studied and discussed in this paper from quantitative angle, and as two independent and coexistent reactions.
从定量角度描述气固相催化反应中内外扩散过程对反应选择性(S)的影响,并以两个独立并存的反应类型的内外扩散过程对S的影响为例进行定量讨论。
5) solid-phase chemical reaction
固相化学反应
1.
Synthesis of zinc phosphate micro-crystal bars by solid-phase chemical reaction at low temperature;
低热固相化学反应法合成磷酸锌微米晶棒
2.
Preparation of AlH_3 with mechanical ball-milling solid-phase chemical reaction;
机械球磨固相化学反应制备AlH_3
6) solid-state chemical reaction method
固相化学反应法
1.
Precursor of nano-sized Cu-Mn composite oxide was synthesized by solid-state chemical reaction method with cupric acetate\,manganese acetate\ and oxalic acid\ as the raw materials.
以乙酸铜、乙酸锰与草酸为原料,采用固相化学反应法制备了纳米铜锰复合氧化物前驱物,利用均匀设计考察了微波功率与加热时间、热分解温度及时间对产物粒径的影响。
补充资料：四氧化锇氧化反应
分子式：
CAS号：
性质：利用四氧化锇作氧化剂，对烯烃进行氧化生成顺式1,2-二醇的反应。反应一般在醚溶液中进行，用吡啶作催化剂，先生成环状酯，后者再经亚硫酸氢钠水溶液水解，生成顺式的1,2-二醇。由于四氧化锇价格昂贵，且毒性大，为此可用催化量的四氧化锇，在三级胺氧化物(R3N-O)或氢过氧化叔丁基存在下进行，后者可将反应中生成的低价锇氧化成四氧化锇，重复使用。
CAS号：
性质：利用四氧化锇作氧化剂，对烯烃进行氧化生成顺式1,2-二醇的反应。反应一般在醚溶液中进行，用吡啶作催化剂，先生成环状酯，后者再经亚硫酸氢钠水溶液水解，生成顺式的1,2-二醇。由于四氧化锇价格昂贵，且毒性大，为此可用催化量的四氧化锇，在三级胺氧化物(R3N-O)或氢过氧化叔丁基存在下进行，后者可将反应中生成的低价锇氧化成四氧化锇，重复使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条