1) many aging
多次时效
2) secondary ageing
二次时效
1.
The secondary ageing time has little effect on the mechanical properties of the alloy.
二次时效温度高于100℃时,合金的主要强化相由θ′相逐渐转变为Ω相。
2.
The influence of secondary ageing on the mechanical properties of 7055 Al alloy was investigated on the basis of Vickers hardness measurement, tensile test and Kahn tear test.
利用维氏硬度和拉伸力学性能测试、Kahn撕裂试验等方法,研究二次时效对7055铝合金力学性能的影响。
3.
Based on TEM and SEM observation, the effect of secondary ageing on microstructures and Kahn tear fractographs of 7055 Al alloy was investigated.
利用透射电镜和扫描电镜研究了二次时效处理后7055合金显微组织及Kahn撕裂断口形貌特征。
3) two step aging
两次时效
4) myopic defocus
短时多次
5) Multi-artificial Aging
多级时效
1.
Effects of Multi-artificial Aging on Mechanical Properties of Low Pressure Casting A356.2 Aluminum Alloy Wheel
多级时效对低压铸造A356.2轮毂力学性能的影响
6) secondary time effect
次时间效应
补充资料：多苯基多次甲基多异氰酸酯
分子式：C6H4(NCO)CH2C6H4(NCO)C8H5NO)X
分子量：350-400
CAS号：9016-87-9
性质：褐色透明液体。相对密度为1.200，折光率1.6240。蒸气压（25℃）为2.13×10-5kPa。
制备方法：将苯胺和甲醛按摩尔比1.6-2.0：1配合，再配入盐酸作为缩作催化剂，加入缩合器中，于90-110℃反应30-60min，得到一定比例二苯基甲烷-4，4'-二胺和多次甲基多苯基甲胺，再经光气化、分离、提纯即可得PAPI和MDI。原料消耗定额：甲醛（100%）150kg/t、苯胺750kg/t、光气850kg/t。
用途：用于制聚氨酯材料，广泛应物于建筑行业、汽车工业、电器工业等作保温材料或垫褥等。
分子量：350-400
CAS号：9016-87-9
性质：褐色透明液体。相对密度为1.200，折光率1.6240。蒸气压（25℃）为2.13×10-5kPa。
制备方法：将苯胺和甲醛按摩尔比1.6-2.0：1配合，再配入盐酸作为缩作催化剂，加入缩合器中，于90-110℃反应30-60min，得到一定比例二苯基甲烷-4，4'-二胺和多次甲基多苯基甲胺，再经光气化、分离、提纯即可得PAPI和MDI。原料消耗定额：甲醛（100%）150kg/t、苯胺750kg/t、光气850kg/t。
用途：用于制聚氨酯材料，广泛应物于建筑行业、汽车工业、电器工业等作保温材料或垫褥等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条