1) lead dioxide nanosheets
二氧化铅纳米片
1.
With PbNO3 as raw material and K2S2O8 as strong oxidant,lead dioxide nanosheets were successfully synthesized at the first time by low temperature solid-state redox reaction assisted by the anionic surfactant-sodium dodecyl sulfate(SDS) under the alkali condition.
TEM测试结果表明,所得二氧化铅纳米片的平均尺寸为300 nm×200 nm。
2) Nanometer sized lead oxide
纳米氧化铅
3) lead oxide nanorod
氧化铅纳米棒
1.
A simple method to fabricate lead oxide nanorods by electrochemical reduction was introduced.
用电化学还原法制备出氧化铅纳米棒,用SEM、TEM、EDS和XRD研究其微观形貌和晶体结构。
2.
A simple method to fabricate lead oxide nanorods by electrochemical reduction was in- troduced.
用电化学还原法制备出氧化铅纳米棒,用 SEM、TEM、EDS 和 XRD 研究其微观形貌和晶体结构。
4) nanocrystalline Ce-doped PbO2 deposited film modified electrode
掺铈纳米二氧化铅修饰电极
1.
The nanocrystalline Ce-doped PbO2 deposited film modified electrode showed favorable electrocatalytic behavior toward the monoamine neurotransmitters with relatively high sensitivity and stability.
研制了一种新型掺铈纳米二氧化铅修饰电极,用X射线衍射(XRD)和扫描隧道显微镜(STM)进行了表征。
5) ZnO nano-sheets
氧化锌纳米片
6) nickel oxide nanosheet
氧化镍纳米片
补充资料：二氧化铅
PbO2 又称过氧化铅、铅酸酐，一种强氧化剂。棕褐色粉末，晶体结构属斜方晶系。受光的作用分解成四氧化三铅和氧。加热到290℃时生成三氧化二铅和氧,继续升温则分解成四氧化三铅和氧。不溶于水和乙醇，溶于盐酸。与有机物接触易燃。
二氧化铅在自然界中以块状黑铅矿存在。人工制取方法有:①铅盐溶液进行阳极氧化制得,此法多用以制备二氧化铅电极。②在碱性溶液中,以氯氧化红丹(Pb3O4)制得;或以氯、溴、次氯酸等氧化其他二价铅盐制得;还可用过氧化钠、过（二）硫酸盐等作为氧化剂，与四氧化三铅的悬浮液作用制得。
二氧化铅在铅－酸蓄电池中用作阳极板的活性材料，在染料中用作氧化剂，在含硫聚合物、烷基苯、乙醛等有机化合物反应过程中用作催化剂，还用于烟火、火柴的制造。因二氧化铅有毒，在生产时要注意防护，在空气中的最大容许剂量为0.05mg/m3。
二氧化铅在自然界中以块状黑铅矿存在。人工制取方法有:①铅盐溶液进行阳极氧化制得,此法多用以制备二氧化铅电极。②在碱性溶液中,以氯氧化红丹(Pb3O4)制得;或以氯、溴、次氯酸等氧化其他二价铅盐制得;还可用过氧化钠、过（二）硫酸盐等作为氧化剂，与四氧化三铅的悬浮液作用制得。
二氧化铅在铅－酸蓄电池中用作阳极板的活性材料，在染料中用作氧化剂，在含硫聚合物、烷基苯、乙醛等有机化合物反应过程中用作催化剂，还用于烟火、火柴的制造。因二氧化铅有毒，在生产时要注意防护，在空气中的最大容许剂量为0.05mg/m3。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。