1) Ni-Cu dual single-phase alloy
Ni-Cu二元单相合金
2) Ni、Mo、Cu alloy element
Ni、Mo、Cu合金元素
3) nickel-copper-phosphorus ternary alloy
Ni-Cu-P三元合金
4) binary two-phase alloy
二元双相Cu-Cr合金
5) Cu-Ni alloy
Cu-Ni合金
1.
By using 3-amino-1,2,4-triazole (ATA) as metal treatment reagent,the self- assembled monolayers (SAMs) were prepared on the surface of Cu-Ni alloy,and its anticorrosion and adsorption mechanism have been investigated by electrochemical method.
利用3-氨基-1,2,4-三氮唑(ATA)金属处理剂在Cu-Ni合金表面制备了自组装单分了膜(SAMs),用电化学方法研究ATA SAMs对Cu-Ni合金的缓蚀作用及其吸附行为。
2.
And the critical technological condition, structure and properties of the mono-phase solid solution of Cu-Ni alloy made by powder co-oozing are investigated.
用固相烧结法将铜粉和镍粉制成块状试样,用OM,SEM和X-射线衍射等方法分析混合粉的扩散过程,研究铜粉和镍粉通过固相扩散形成单相Cu-Ni固溶体合金的临界工艺条件、共渗Cu-Ni合金的结构特征和性能特点。
6) Cu-Ni-Be alloy
Cu-Ni-Be合金
1.
Treating by the process of merging vacuum brazing and quenching into one and then aging treatment,the effect of holding time on structures and properties of Cu-Ni-Be alloy and bonding is studied.
通过SEM、EDS、金相显微镜及拉伸试验分析了不同钎焊温度下钎焊接头的显微组织及性能特征,研究了保温时间对经真空钎焊、淬火复合工艺及时效处理后母材Cu-Ni-Be合金和接头组织及性能的影响。
补充资料：Cu-A1-Ni shape memory alloy
分子式：
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。