1) CdS/PPA nanoparticles
CdS/PPA纳米粒子
2) CdS nanoparticles
CdS纳米粒子
1.
Effect of different preparation condition on the qua ntum size effect of the CdS nanoparticles;
工艺条件对CdS纳米粒子量子尺寸效应的影响
2.
The synthesis and characterization of CdS nanoparticles;
CdS纳米粒子的合成方法
3.
CdS nanoparticles is a kind of important semiconductor nano-materials and has drawn much attention recently due to their much potential applications in many fields,such as photoelectricity,magnetism,catalyst,bioanalysis,etc.
CdS纳米粒子作为一种重要的半导体纳米材料,因其在光、电、磁、催化等方面具有巨大的应用潜能。
3) CdS nanoparticle
CdS纳米粒子
1.
CdS nanoparticles were directly synthesized in aqueous solution at room temperature.
室温条件下在水溶液中合成了粒度分布均匀、分散性好的CdS纳米粒子。
2.
The surfacemodified CdS nanoparticle (named as CdS/AOTSO- 3) with surfactant, AOT, was synthesized by reverse micelle method.
用反胶束法合成了用表面活性剂分子磺基琥珀酸双 2 乙基己酯钠盐 (AOT)进行表面修饰的CdS纳米粒子 (记为CdS/AOT SO-3) ,研究了这种纳米粒子在正庚烷(heptane)和吡啶 (Py)溶剂中的荧光及光解行为 。
3.
The CdS nanoparticles were synthesized by thioacetamide (TAA) and cadmium nitrate (Cd(NO3)2) in the alkaline solution,and the nanoparticles proved to be stable in the aqueous solution.
室温条件下在水溶液中以硫代乙酰胺和硝酸镉为原料,采用微波法合成了粒度分布均匀、分散性好的CdS纳米粒子,在pH7。
4) CdS nanocomposites
CdS纳米复合粒子
1.
The SPAn/CdS nanocomposites were prepared by solvothermal method.
采用溶剂热法,成功的制备了磺化聚苯胺(SPAn)包裹CdS纳米复合粒子。
5) CdS nanoparticle
CdS纳米微粒
1.
CdS nanoparticles were prepared in a room temperature ionic liquid,1-methyl-3-hexyl-imidazolium tetrafluoroborate.
合成了1-甲基-3-己基咪唑四氟硼酸盐离子液体,并以此为反应介质通过有机金属化合物热分解法制备出CdS纳米微粒,采用X射线粉末衍射仪和透射电子显微镜对CdS纳米微粒的结构和形貌进行表征,在四球摩擦磨损试验机上考察了含CdS纳米微粒离子液体的摩擦磨损行为。
2.
And then, Cd(MA)2 was polymerized via surface-initiated ATRP on the surface of α-Br groups modified PS spheres, CdS nanoparticles were formed in situ by bubbling H2S gas.
结合表面引发的原子转移自由基聚合和气/固反应制备CdS纳米微粒/聚苯乙烯核壳微球。
3.
CdS nanoparticles were prepared in a room temperature ionic liquid, 1-methyl-3-hexyl-imidazolium tetrafluoroborate.
合成了1-甲基-3-己基咪唑四氟硼酸盐离子液体,以所合成的离子液体为反应介质通过有机金属化合物热分解法制备了CdS纳米微粒。
6) CdS nanoparticles
CdS纳米颗粒
1.
Preparation of CdS nanoparticles by reverse micelle method;
通过研究CTAB四元反相胶团体系的成相区域、稳定性、微液滴大小和尺寸分布和胶团组成,得出了反相胶团组成与胶团中微液滴大小的关系,采用TEM、XRD等分析技术对所制备的CdS纳米颗粒进行了性能表征。
补充资料：PPA
分子式：
CAS号：
性质：又称聚邻苯二甲酰邻苯二胺树脂。含邻苯二甲酰胺结构的酰胺聚合物。商品名Amodel。机械强度和热稳定性好；吸水率(24h)0.2％；耐磨性和耐疲劳性优于脂肪族聚酰胺。有注塑级、挤塑级、吹塑级、阻燃级、增强级和超韧级等系列产品。超韧级产品，在50％相对湿度下悬臂梁(Izod)冲击强度(缺口)1200J/m。45％玻纤增强PPA，在50％相对湿度下弯曲强度310MPa，弯曲模量>18.8GPa，较聚酰胺66和PPS高75％；热变形温度185℃。由邻苯二甲酸与邻苯二胺缩聚制得。可用作汽车、化工设备、电动工具、机械、仪器仪表、宇航、兵器的零部件。
CAS号：
性质：又称聚邻苯二甲酰邻苯二胺树脂。含邻苯二甲酰胺结构的酰胺聚合物。商品名Amodel。机械强度和热稳定性好；吸水率(24h)0.2％；耐磨性和耐疲劳性优于脂肪族聚酰胺。有注塑级、挤塑级、吹塑级、阻燃级、增强级和超韧级等系列产品。超韧级产品，在50％相对湿度下悬臂梁(Izod)冲击强度(缺口)1200J/m。45％玻纤增强PPA，在50％相对湿度下弯曲强度310MPa，弯曲模量>18.8GPa，较聚酰胺66和PPS高75％；热变形温度185℃。由邻苯二甲酸与邻苯二胺缩聚制得。可用作汽车、化工设备、电动工具、机械、仪器仪表、宇航、兵器的零部件。