1) double emulsion-solvent evaporation
复乳法-液中干燥法
1.
Bovine serum albumin(BSA) loaded poly(ethylene glycol)-block-poly(ε-caprolactone-cobenzyl(7-oxooxepan-2-yl) acetate)(PEBCL) microcapsule was prepared by W/O/W double emulsion-solvent evaporation technique.
采用复乳法-液中干燥法制备了一系列含有牛血清蛋白(BSA)的聚乙二醇-b-聚(6-(乙酸苄酯)-ε-己内酯-co-ε-己内酯(PEBCL)微囊。
2) o/w emulsion in-liquid drying process
o/w型乳化-液中干燥法
3) o/o emulsion in-liquid drying process
o/o型乳化-液中干燥法
1.
The biodegradable sustained-release microspheres loaded with huperzine A for injection were prepared by o/w and o/o emulsion in-liquid drying process, respectively.
对比研究了o/w型和o/o型乳化-液中干燥法制得微球的形态、粒径和药物体内外释药情况。
4) in-liquid drying method
液中干燥法
1.
In this paper,2,4,6-triiodophenol-ethylcellulose-microsphere was developed by in-liquid drying method,in order to increase the granularity of the X-ray CT contrast agent and to prevent the blood vessel X-ray CT contrast agent from exuding through the vascular wall to the tissue.
为提高造影剂的颗粒度,减少血池造影剂透过血管壁向组织间质渗出,影响血池造影剂的造影效果,采用液中干燥法制备了三碘苯酚乙基纤维素微球,研究了三碘苯酚与乙基纤维素的质量比对微球成球性、粒径以及载药量的影响,发现两者的质量比为1∶2时成球性最好,所得微球为规整的球形,微球粒径最小,平均粒径D50为3。
5) Emulsion freeze-drying
乳液冷冻干燥法
6) liquid desiccant method
溶液干燥法
1.
Drying of gel cast parts of BaTiO_3-based semiconduting ceramics via the liquid desiccant method was studi.
将PEG(聚乙二醇)溶液干燥法应用于BaTiO3半导瓷注凝成型坯体的干燥,由于PEG溶液可以和坯体的所有表面接触,因此可提供更均匀的干燥介质,从而减小在干燥过程中产生的应力。
补充资料：乳液纺丝法
分子式：
分子量：
CAS号：
性质：一种新型的纺丝方法。是将聚合物以乳液形态分散于某种可纺性较好的物质（称作载体）中，然后将载体按常用的纺丝方法纺丝成形。得到的初生纤维经拉伸后在高温下烧结，载体被炭化，从而得到所要求的聚合纤维。此法适于那些分解温度比熔点低，又没有合适的溶剂溶解或塑化的聚合物纺丝成形，如聚四氟乙烯纤维的纺制等。载体常用粘胶或聚乙烯醇水溶液，所以此法在工艺上类似于湿法纺丝。
分子量：
CAS号：
性质：一种新型的纺丝方法。是将聚合物以乳液形态分散于某种可纺性较好的物质（称作载体）中，然后将载体按常用的纺丝方法纺丝成形。得到的初生纤维经拉伸后在高温下烧结，载体被炭化，从而得到所要求的聚合纤维。此法适于那些分解温度比熔点低，又没有合适的溶剂溶解或塑化的聚合物纺丝成形，如聚四氟乙烯纤维的纺制等。载体常用粘胶或聚乙烯醇水溶液，所以此法在工艺上类似于湿法纺丝。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条