1) soda-lime sintering process
碱石灰烧结法
1.
Using soda-lime sintering process-alkali leaching process,under the sintering conditions of temperature 1 250℃,time 120 minutes,calcium-silicon ratio 2.
采用碱石灰烧结法—碱浸工艺,在温度1250℃、时间120 min、配料钙硅比为2。
2) Deville Pechiney process
碱石灰烧结法<冶>
3) lime sintering process
石灰烧结法
1.
Based on the Chinese bauxite character,the mechanism of intensified lime sintering process was studied different from traditional sintering process.
针对我国资源特点,本文提出不同于传统的石灰烧结法的强化石灰烧结法机理,采用铝硅比为3。
2.
After a lot of tests,it proves that it is feasible to produce potassium and aluminium products with potassium slate by lime sintering process.
经过大量试验,证实了用石灰烧结法处理富钾板岩生产钾铝产品的工艺是可行的。
4) caustic-lime method
烧碱石灰乳法
5) natronkalk
['neitrən'kɔ:k]
烧碱石灰
6) sintering method of limestone
石灰石烧结法
1.
Discussing of controlling parameters on the alumina production with sintering method of limestone;
石灰石烧结法生产氧化铝的控制指标探讨
补充资料：碱石灰烧结法
碱石灰烧结法
lime-sode sintering process
一种札化铝生产方法，在拜耳法广泛用于工业生产之后，在工业上本法仅用于处理低品位高硅铝矿物。 简史1858年法国的吕·查德里(Le Chatelier)提出用碳酸钠同铝土矿烧结，溶出烧结产物后将得到的铝酸钠溶液通二氧化碳气分解，析出氢氧化铝;再将氢氧化铝锻烧成氧化铝，于1860年制得首批氧化铝。在当时西方国家的一些文献中，将烧结法称为吕·查德里法。用这种方法处理含氧化硅较高的铝土矿时，氧化铝和碱的损失很大。1880年缪勒(G.Muller)提出在烧结配料中加入石灰石以减少氧化铝和碱的损失。1902年巴卡尔德(H.Paekard)确定lmol510:配入Zmol CaO的配料方案。后来就一直沿用这一配料方案，即NaZO:A1203=1，CaO:5102“2。但至1911年拜耳法专利期满之后，碱石灰烧结法即不再用于处理高品位铝土矿。 前苏联最初发现的铝矿为低品位铝土矿，为此于1932年和1938年分别建成采用干式烧结和湿式烧结的碱石灰烧结法氧化铝厂。从20世纪50年代到60年代又相继建成处理霞石的J ianshihui shaoiiefa碱石灰烧结法(lime一soda sintering proeess) 用纯碱及石灰石与铝矿物共同烧结处理铝矿石的烧结法工厂。中国在1954年建成用烧结法处理铝土矿的山东铝厂。这样，碱石灰烧结法在一些高品位铝土矿资源有限而低品位铝土矿或其他高硅铝冶金原料丰富的国家，又获得了应用，工艺技术也日趋完善。 工艺主要由破碎、细磨、烧结(见招酸盐炉抖烧结)、熟料溶出(见铝酸盐熟朴溶出)、赤泥分离(见赤泥分离与洗涤)、脱硅(见铝酸钠溶液脱硅)、碳酸化分解(见铝酸钠溶液破酸化分解)和加种子分解(见铝酸钠溶液加种子分解)、缎烧(见氮或化铝傲烧)等过程组成(见图)。 破碎后的铝土矿和石灰按规定比例送入磨机，并配入一定数量经燕发的碳酸化分解母液和新的纯碱进行细磨。磨细后的料浆需进行调整，以保证符合配料要求。