1) Al2O3/Cu compound layer
Al2O3/Cu表面复合层
1.
Al2O3/Cu compound layer was prepared through internal oxidation of aluminized copper.
利用纯铜渗铝-内氧化工艺制备了Al2O3/Cu表面复合层,测试了表层的组织结构和力学性能,并进行了黏着磨损、固定磨料磨损和松散磨料振动与非振动情况下的磨损试验。
2) Al 2O 3/Cu surficial composite layer
Al2O3/Cu表面复合材料
3) Al2O3/Cu composites layer
A12O3/Cu表面复合层
1.
Influence of the aluminum in aluminizing agents on the aluminum distribution in the copper surface is discussed, the microstructure and properties of Al2O3/Cu composites layer under different technical parameter are studied.
本文采用包埋法纯铜渗铝-内氧化工艺制备A12O3/Cu表面复合层,考察了渗剂中铝含量对表面渗层中铝含量分布的影响,并对采用不同工艺参数条件下获得的A12O3/Cu表面复合层的显微组织和性能进行了相关研究。
4) Cu/WC P composite coating
Cu/WCP表面复合涂层
5) Al_2O_3/Cu composite
Al2O3/Cu复合材料
1.
Using self-made electric-tribo tester,electric-tribological behaviors of Al_2O_3/Cu composites by internal oxidation were investigated.
采用内氧化法制备Al2O3/Cu复合材料,在自制电磨损试验机上评价Al2O3/Cu复合材料的磨损性能,采用扫描电子显微镜观察Al2O3/Cu复合材料的磨损表面形貌,用能谱仪对其磨损表面主要元素进行分析并探讨其磨损机制。
2.
Al_2O_3/Cu composites were prepared by internal oxidation of Cu-Al alloy.
采用简化的内氧化工艺制备了Al2O3/Cu复合材料,研究不同内氧化时间(3～10h)及不同变形量(20%～80%)下的Al2O3/Cu复合材料的显微硬度和导电率,并对其显微组织进行了分析。
6) Cu-Al2O3/Cr composite
Cu-Al2O3/Cr复合材料
1.
Cu-Al2O3/Cr composite was prepared by powder metallurgy.
用粉末冶金方法制备了Cu-Al2O3/Cr复合材料,研究了压制力(200、250、300、350 MPa)对烧结件显微组织的影响以及该复合材料的密度、硬度、导电率的变化。
补充资料：Al-Cu cast aluminium alloy
分子式：
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。