1) co-based matrix material
钴基胎体材料
2) Cobaltbased matrix
钴基胎体
3) matrix material
胎体材料
1.
The process for preparing electrodeposited diamond tools by using nanocrystalline Ni-Co alloy deposit as a new matrix material and the features are presented.
介绍了采用纳米镍-钴镀层作为新型胎体材料,制备电镀金刚石工具的方法及其特点。
4) matrix materials
胎体材料
1.
Experimental research on erosion and corrosion of WC-base matrix materials for drill bits under impingement of drilling mud;
泥浆对钻头WC基胎体材料冲蚀磨损的试验研究
2.
One important index of the working life and performance of diamond tools is the retention intensity of diamonds in the diamond tools,to a great extent,the high-effective applying of which is determined by the mechanical properties of the matrix materials in the actual practice.
金刚石工具工作寿命和性能的一个重要指标就是金刚石在金刚石工具中的把持强度,其在实际工作中的使用效果在很大程度上取决于胎体材料的性能。
5) matrix
[英]['meɪtrɪks] [美]['metrɪks]
胎体材料
1.
Diamond was used as abrasive and Ni-Mn alloy as matrix material.
本文采用复合电镀工艺,用金刚石做磨料,镍锰合金作胎体材料,研制和生产耐磨金刚石滑履,金刚石的品级为MBD4,粒度是0。
2.
Nickel - Cobalt alloy is used as matrix material.
为了满足导垂孔施工孔径大、垂直精度高(孔斜允许偏差在1‰以内)的要求,本文采用复合电镀技术研制出大口径金刚石钻头,所用胎体材料为镍钴合金,钻进金刚石的品级为MBD8、MBD10,其中MBD10占总量的60％,金刚石粒度分别为40／45、45／50、50／60、60／70,各种粒度的比例(质量比)分别为20％、30％、35％、15％。
3.
The influence of carbide forming element Ti and Cr on bondingstrength between matrix and diamond were investigated.
Ti 和 Cr 可以改善胎体材料对金刚石的润湿和粘结。
6) Co-based wires
钴基丝状材料
补充资料：先驱体法碳化硅纤维增强铝基复合材料
分子式：
CAS号：
性质：一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维，与铝复合后一般含纤维40％(体积)左右，单向增强时纵向拉伸强度约为700～1000MPa，模量95～120GPa，密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润，常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝，然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细，柔曲性好，此便于制造形状比较复杂的零件。
CAS号：
性质：一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维，与铝复合后一般含纤维40％(体积)左右，单向增强时纵向拉伸强度约为700～1000MPa，模量95～120GPa，密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润，常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝，然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细，柔曲性好，此便于制造形状比较复杂的零件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。