1) Zn-Mg-Al hydrotalcite-like materials(LDHs)
Zn-Mg-Al类水滑石
1.
Zn-Mg-Al hydrotalcite-like materials(LDHs) were synthesized by a coprecipition method and characterized by XRD,IR to prove its hydrotalcite-like structure.
采用共沉法制备Zn-Mg-Al类水滑石并且利用XRD,IR等手段对催化剂进行表征,研究Zn-Mg-Al类水滑石及其焙烧产物对酯交换反应的催化活性。
2) Zn-Al HTALs
Zn-Al类水滑石
1.
46 mg P·g-1 in sludge filtrate of a sewage work by Zn-Al HTALs was obtained when the adsorbent was prepared at 70℃ using NaOH solution as the coprecipitant,aged for 6 h and calcined at 300℃ for 4 h.
采用共沉淀法制备了一系列Zn-Al类水滑石吸附剂,并考察了制备条件对其磷酸盐吸附性能的影响。
3) Mg-Al-hydrotalcite-like compound
Mg-Al类水滑石
1.
The influence of pH value on the viscosity of cationic starch(CS) solution, the mass ratio(R) of Mg-Al-hydrotalcite-like compound(Mg-Al-HTlc) to CS and the pH value on the viscosity of CS/HTlc suspension were studied.
研究了阳离子淀粉(CS)/Mg-Al类水滑石(HTlc)悬浮体系的粘度行为。
4) Ca/Mg/Al hydrotalcite like compouds
Ca/Mg/Al类水滑石
5) Zn/Al Hydrotalcite
Zn/Al水滑石
6) Mg-Al LDHs
Mg-Al水滑石
1.
Hydrothermal Synthesis Nano Mg-Al LDHs and its Formation Mechanism;
纳米晶Mg-Al水滑石的水热合成及合成机理
2.
Microwave-hydrothermal Synthesis and Characterization of Nano Mg-Al LDHs;
微波水热法制备Mg-Al水滑石纳米晶
补充资料：Al-Zn east aluminium alloy
分子式：
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。