1) near-β TB10 titanium alloy
近β型TB10钛合金
2) TB10 titanium alloy
TB10钛合金
1.
FEM simulation of backward extrusion process of TB10 titanium alloy cylinder
TB10钛合金筒体反挤压成形的有限元模拟
3) near β type titanium alloys
近β型钛合金
4) near β titanium alloy
近β钛合金
1.
Objective:This study was intended to modify the surface of a novel near β titanium alloy Ti-5Zr-3Sn-5Mo-15Nb (TLM) by micro-arc oxidation(MAO),and evaluate the influence of MAO process on the morphology and integrin β1(Itgβ1) expression of osteoblasts cultured on TLM.
目的:采用微弧氧化(MAO)方法对近β钛合金Ti-5Zr-3Sn-5Mo-15Nb(TLM)进行表面处理,观察其对成骨细胞在其表面粘附形态及整合素表达水平的影响。
2.
The objective of this study was to modify the surface of a novel near β titanium alloy Ti-5Zr-3Sn-5Mo-15Nb (TLM) by micro-arc oxidation (MAO).
采用微弧氧化(MAO)方法对近β钛合金Ti-5Zr-3Sn-5Mo-15Nb(TLM)表面进行处理,分析其表面特性变化,并观察成骨细胞在其表面的早期粘附。
5) β-type titanium alloys
β型钛合金
1.
The aim of the study is to evaluate the in vivo biocompatibility to two novel β-type titanium alloys:TLE (Ti-(3～6)Zr-(2～4)Mo(24～27)Nb), TLM 2(Ti-(1.
通过皮下、肌肉植入试验评价两种β型钛合金材料TLE(Ti-(3～6)Zr-(2～4)Mo(24～27)Nb),TLM2(Ti-(1。
6) biomedical β-type Ti alloys
医用β型钛合金
补充资料：近β钛合金
分子式：
CAS号：
性质： β稳定元素略高于临界浓度的钛合金。成分中主要含有β稳定元素钒、钼、铁、铬等。具有最高的强化效应、最高的强度(1200MPa)、较深的淬透截面(60～150mm)、良好的拉伸塑性和断裂韧性。主要有β-Ⅲ、BT22等牌号。采用真空自耗电弧炉熔炼制取。适于制造紧固件和较大截面的模锻件。