1) zirconium alloy (NZ2)
新锆合金(NZ2)
3) Zr-Sn-Nb alloy (N18 alloy)
N18(NZ2)合金
4) new zirconium alloy
新锆合金
1.
Research on hot rolling process for new zirconium alloy;
新锆合金热轧工艺的研究
2.
The microstructure of oxide film for new zirconium alloys was studied.
研究了氧化膜的微观组织结构,研究结果表明,对采用不同热处理的两种新锆合金,无论从内到外,氧化膜结构均极为相似;不同热处理对氧化膜结构影响在于是否有第二相易于嵌入ZrO2中,累计退火参数值越高,嵌入可能性大;该嵌入的沉淀相促进氧化膜从其它结构到单斜结构的转变,残留于原金属晶界处的第二相促使晶界开裂。
3.
The structure and corrosion resistance of 8 #new zirconium alloy are studied.
研究了８＃新锆合金的组织与耐蚀性能。
5) Zr-Sn-Nb new zirconium alloys
Zr-Sn-Nb新锆合金
1.
The specimens of Zr-Sn-Nb new zirconium alloys were treated in different ways at 1 045 ℃/40 min+500 ℃/1.
5 h工艺,将Zr-Sn-Nb新锆合金加工成厚度为1。
6) zirconium and zirconium alloy
锆及锆合金
1.
Based on the analysis of welding properties of zirconium and zirconium alloys,and through the welding test and research,the zirconium and zirconium alloy piping welding process has been obtained and summarized,and the welding technical specification was also stipulated.
在对锆及锆合金材料焊接性能进行分析的基础上,通过焊接试验研究,摸索和总结出锆及锆合金管道焊接工艺,制定相应的焊接工艺评定,为锆及锆合金材料的焊接积累了丰富的经验。
补充资料：锆4合金
分子式：
CAS号：
性质：锆(锡)合金的一种。标准组成为：锆-1.5%锡-0.2%焰铁-0.1%铬，都有良好的热膨胀系数和热中子吸收截面。抗拉强度63MPa，屈服强度53MPa，伸长率15％，洛氏硬度85。采用真空自耗电极熔炼方法制取。用作水冷动力堆的包壳、燃料组件盒等。
CAS号：
性质：锆(锡)合金的一种。标准组成为：锆-1.5%锡-0.2%焰铁-0.1%铬，都有良好的热膨胀系数和热中子吸收截面。抗拉强度63MPa，屈服强度53MPa，伸长率15％，洛氏硬度85。采用真空自耗电极熔炼方法制取。用作水冷动力堆的包壳、燃料组件盒等。