1) ultra-low carbon and sulphur
超低碳硫
2) Lowcarbon Midsulphur
低碳中硫
4) ULC steel
超低碳钢
1.
Study on the optimum process of refining ULC steel by RH degasser
RH冶炼超低碳钢的最优工艺研究
2.
Inclusions and total oxygen content in ultra-low carbon(ULC) steel were studied for the control of cluster inclusions in ULC steel.
为控制超低碳钢中的簇状夹杂物,对超低碳钢中的夹杂物和与全氧含量的关系进行了研究。
3.
The polarization curve of the ULC steel with titanium and niobium was measured to determine the suitable electrolytic parameters for preparation of TEM carbon replica samples.
测定了一种复合添加钛、铌超低碳钢的极化曲线,选用合适的电流密度和电解时间以碳复型方法萃取钢中的析出相制备透射电镜观察用样品。
5) ultra-low-carbon steel
超低碳钢
1.
Development on ultra-low-carbon steel mold powder of Baosteel;
宝钢超低碳钢保护渣的开发
2.
Effect of Mould Shielded Fluxes on Concasting Billet Surface Carbonization of Ultra-Low-Carbon Steel;
结晶器保护渣对超低碳钢连铸坯表面渗碳的影响
3.
Composite Treatment of Concasting Mold Flux for Ultra-Low-Carbon Steel;
超低碳钢连铸结晶器用保护渣的超细复合处理
6) ultra low carbon
超低碳
1.
Effect of Control Rolling and Aging on Structure and Properties of 570 MPa Ultra Low Carbon Bainitic Steel;
控轧和时效对570 MPa超低碳贝氏体钢组织和性能的影响
2.
Microstructure, properties and boron distribution of HAZ in an ultra low carbon bainitic Cu containing steel were investigated by welding simulation on a Gleeble 1500 thermal simulator.
用Gleeble1500热模拟机对含铜超低碳贝氏体钢进行不同焊接工艺下热模拟试验。
补充资料：超低碳不锈钢
分子式：
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。