1) thick-wall stainless steel clad plate
厚壁不锈钢复合板
1.
This paper introduces the welding procedure of 16MnR/316L stainless steel clad plate with ceramic backing,submerged arc welding and flux-cored wire CO2 automatic welding,which is used to resolve the welding and heat treatment problems of thick-wall stainless steel clad plate,the welding procedure is proved feasible,it has been applied in industry successfully.
介绍了采用陶瓷衬垫、埋弧机械化焊、药芯焊丝CO2自动焊来焊接16MnR/316L不锈钢复合板的焊接工艺,解决了厚壁不锈钢复合板的焊接和热处理问题;通过检查焊缝的化学成分和力学性能等,证明了该焊接工艺的可行性,并成功应用于生产中。
2) big and thick stainless steel/carbon steel clad plate
中厚不锈钢/钢复合板
3) Stainless Steel Compound Plate
不锈钢复合钢板
1.
On Welding of Stainless Steel Compound Plate 16MnR+00Cr19Ni10;
16MnR+00Cr19Ni10不锈钢复合钢板的焊接
4) Stainless Steel-steel
不锈钢-钢复合板
5) composite stainless steel plate
复合不锈钢板
6) stainless steel clad plate
不锈钢复合板
1.
According to clad metal characteristics,the welding experiment of stainless steel clad plate 16MnR+316L are conducted,from what has been done above,the welding practice is made up,the welding quality is guaranteed and the welding efficiency is increased.
根据不锈钢复合板的特性,分析了16MnR+316L不锈钢复合板的焊接性,对焊接工艺进行了评定试验,确定了焊接工艺,保证了设备的焊接质量,提高了焊接效率。
2.
The stainless steel clad plate,whose base is 20MnMoNb and cladding is import 304 steel plate,appears serious crack after a large explosion,but its cladding doesn't crack.
基层为20MnMoNb、复层为进口304钢板的不锈钢复合板,其爆炸后基层出现了严重开裂,但复层未裂的问题。
补充资料：不锈钢板
分子式：
分子量：
CAS号：
性质：按制法分热轧和冷轧的两种，包括厚度0.5-4毫米的薄板和4.5-35毫米的厚板。按钢种的组织特征分为5类：奥氏体型、奥氏体-铁素体型、铁素体型、马氏体型、沉淀硬化型。要求能承受草酸、硫酸-硫酸铁、硝酸、硝酸-氢氟酸、硫酸-硫酸铜、磷酸、甲酸、乙酸等各种酸的腐蚀，广泛用于化工、食品、医药、造纸、石油、原子能等工业，以及建筑、厨具、餐具 、车辆、家用电器各类零部件。为了保证各类不锈钢板的屈服强度、抗拉强度、伸长率和硬度等力学性能符合要求，钢板交货前必须经过退火、固溶处理、时效处理等热处理。
分子量：
CAS号：
性质：按制法分热轧和冷轧的两种，包括厚度0.5-4毫米的薄板和4.5-35毫米的厚板。按钢种的组织特征分为5类：奥氏体型、奥氏体-铁素体型、铁素体型、马氏体型、沉淀硬化型。要求能承受草酸、硫酸-硫酸铁、硝酸、硝酸-氢氟酸、硫酸-硫酸铜、磷酸、甲酸、乙酸等各种酸的腐蚀，广泛用于化工、食品、医药、造纸、石油、原子能等工业，以及建筑、厨具、餐具 、车辆、家用电器各类零部件。为了保证各类不锈钢板的屈服强度、抗拉强度、伸长率和硬度等力学性能符合要求，钢板交货前必须经过退火、固溶处理、时效处理等热处理。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条