1) aesthetic transmutation
审美嬗变
1.
Reversing the traditional production of movies or TV series from ready-made novels,the new form helps to turn out a combined TV(movie)-novel text which changes people s traditional way of novel reading and completes the aesthetic transmutation in an"era of pictures.
这种文学现象打破传统由小说到影视的改编过程,而是将二者倒置,产生了图文并茂的“影视小说读本”,从而改变了人们的传统阅读习惯,反映了影像时期小说的审美嬗变。
2) The Change of Taste in Ci
词的审美嬗变
4) The Diversification of Aesthetic Experience
审美经验的递嬗
5) On the Evolution of American Education
美国教育的嬗变
6) evolution
[英][,i:və'lu:ʃn] [美]['ɛvə'luʃən]
嬗变
1.
Evolution of the Social Customs in Jiangsu after the Chinese Revolution of 1911 - 1912;
革命后江苏社会风俗的嬗变
2.
Traditional Development and Evolution to the Poetic Styles of Yong Shi Poem——Discussion on Zuo Si s Eight Pieces of Yong Shi Poems;
“咏史”诗体传统的开拓与嬗变——论左思《咏史诗》八首
3.
On the evolution of the content of Taoist stories in the Six Dynasties;
论汉魏六朝道教小说内容的嬗变
补充资料:半导体核嬗变掺杂
用一定能量的中子、带电粒子或γ射线等照射材料,通过选择的核反应在基体中生成原来不存在的新元素,达到半导体材料的掺杂目的。目前,只有中子嬗变掺杂(NDT)得到了实际应用。此方法的原理是K.拉克-霍罗维茨于1951年提出的。1974年成功地用核反应堆热中子对区熔硅进行核嬗变掺杂,首次生产了商品的中子嬗变掺杂硅。目前中子掺杂硅单晶已成为工业产品,产量逐年增加。
超纯硅在反应堆内主要同热中子发生如下核反应。此反应生成的稳定31P就是N型硅希望掺入的施主元素,经照射后达到的31P浓度N1(单位:厘米-3)可用公式
计算。式中N2为硅核30Si的数密度(厘米-3);σ为30Si的热中子辐射俘获截面(0.11靶恩);嗞为热中子注量率(厘米-2·秒-1);t为照射时间(秒)。
核嬗变掺杂的突出优点是掺杂精度高和引入的杂质分布均匀。但反应堆的快中子和γ射线还会同时在硅中造成许多辐照缺陷,使硅的物理性能发生显著变化。研究表明,为恢复硅的电学性能,需经800~900℃的退火处理。
半导体核嬗变掺杂的主要限制之一是残余放射性,对于中子掺杂区熔硅,这主要来源于放射性同位素32P(半衰期为14.3天) 。因此,照射后的样品需经一定时间的辐射冷却,方可作为非放射性材料操作。
目前,对核嬗变掺杂的研究主要集中在辐照技术、辐照缺陷的本质和退火行为以及扩大应用的可能性等问题。
超纯硅在反应堆内主要同热中子发生如下核反应。此反应生成的稳定31P就是N型硅希望掺入的施主元素,经照射后达到的31P浓度N1(单位:厘米-3)可用公式
计算。式中N2为硅核30Si的数密度(厘米-3);σ为30Si的热中子辐射俘获截面(0.11靶恩);嗞为热中子注量率(厘米-2·秒-1);t为照射时间(秒)。
核嬗变掺杂的突出优点是掺杂精度高和引入的杂质分布均匀。但反应堆的快中子和γ射线还会同时在硅中造成许多辐照缺陷,使硅的物理性能发生显著变化。研究表明,为恢复硅的电学性能,需经800~900℃的退火处理。
半导体核嬗变掺杂的主要限制之一是残余放射性,对于中子掺杂区熔硅,这主要来源于放射性同位素32P(半衰期为14.3天) 。因此,照射后的样品需经一定时间的辐射冷却,方可作为非放射性材料操作。
目前,对核嬗变掺杂的研究主要集中在辐照技术、辐照缺陷的本质和退火行为以及扩大应用的可能性等问题。