1) Super high strength magnesium alloys
超高强度镁合金
2) high strength magnesium alloys
高强镁合金
1.
At present,the research and development about high strength magnesium alloys have received much attention all over the world,and consequently many researches have been carried out.
综述了高强镁合金的研究开发现状,尤其是通过添加稀土元素、采用快速凝固技术、大塑性变形和镁基复合材料等制备高强度镁合金的研究现状,指出了高强镁合金研究目前还存在的问题和今后的研究重点。
3) ultra-high strength copper alloy
超高强度铜合金
4) ultrahigh strength aluminum alloy
超高强度铝合金
1.
The microstructures of as-deposited and extruded ultrahigh strength aluminum alloys by spray-forming were investigated.
研究了喷射成形Al-Zn-Mg-Cu系超高强度铝合金的沉积态和挤压态的组织,对挤压态合金进行了固溶处理和时效处理,得到了时效硬度曲线,并进行了力学性能测试。
5) ultra high strength aluminum alloy
超高强度铝合金
1.
Research on constitutive relationship for new ultra high strength aluminum alloy;
新型超高强度铝合金本构方程的研究
2.
The flow stress of 7A60 ultra high strength aluminum alloy was studied by isothermal compress test at constant strain rate.
采用等温恒应变速率压缩试验对 7A60超高强度铝合金的流动应力进行了研究。
6) ultra high strength alloy steel
超高强度合金钢
1.
Experiments indicate that under the conditions of high-speed cutting of ultra high strength alloy steels, the interaction between depth of cut a.
应用析因试验设计与均匀试验设计方法,对超高强度合金钢(硬度大于50HRc、抗拉强度σb>1。
补充资料：超轻镁合金
分子式：
CAS号：
性质：主要指镁锂合金，是目前结构金属材料中最轻的一种合金。相对密度为1.30～1.65t/m3，强度较高，特别是压缩屈服强度显著高于其他镁合金。具有良好的塑性和韧性(包括低温韧性)，缺口敏感性小，容易加工和焊接。这类合金按组织不同可分为三类：α型合金(含有4.5％～6.0％锂和5.0％～6.0％铝，余为镁)、α+β型合金(含有7.0％～10.0％锂，4.0％～6.0％铝，余为镁)和β型合金(含有10.0％～11.5％锂，0.5％～1.0％铝，余为镁)。为了提高强度，还往往加入锌、锰、镉、铈等元素。这类合金可以通过热处理进行强化。由于锂的化学性质活泼，熔铸工艺比较复杂；抗蚀性低于其他镁合金，且有较严重的应力腐蚀倾向。
CAS号：
性质：主要指镁锂合金，是目前结构金属材料中最轻的一种合金。相对密度为1.30～1.65t/m3，强度较高，特别是压缩屈服强度显著高于其他镁合金。具有良好的塑性和韧性(包括低温韧性)，缺口敏感性小，容易加工和焊接。这类合金按组织不同可分为三类：α型合金(含有4.5％～6.0％锂和5.0％～6.0％铝，余为镁)、α+β型合金(含有7.0％～10.0％锂，4.0％～6.0％铝，余为镁)和β型合金(含有10.0％～11.5％锂，0.5％～1.0％铝，余为镁)。为了提高强度，还往往加入锌、锰、镉、铈等元素。这类合金可以通过热处理进行强化。由于锂的化学性质活泼，熔铸工艺比较复杂；抗蚀性低于其他镁合金，且有较严重的应力腐蚀倾向。