1) vanadium zirconium blue
钒锆蓝
1.
With the three-component color mixing system,this article attempts to illustrate that glaze of various colors can be made by changing the property relation between the components,namely,zirconium iron pink,praseodymium zirconium yellow,and vanadium zirconium blue.
采用三组分配釉调色方法,通过对锆铁红、镨锆黄、钒锆蓝三种锆系色釉的配色试验,说明改变其三组分的比例关系,可得到多种不同颜色的系列色釉。
2) turquoise pigment
锆钒蓝
1.
The color development mechanism of turquoise pigment was studied by XRD,XPS and spectrophotometer.
锆钒蓝色料是一种稳定的高温釉用色料 ,它具有稳定的锆英石晶体结构。
3) vanadium-zirconium blue
钒-锆蓝
4) V-Zr pigment
钒锆蓝色料
1.
Using micron-sized or nano-sized ZrO2 as raw materials, V-Zr pigment or Co3O4 as colorant, blue ZrO2 ceramics was prepared through conventional ceramic process.
以微米或纳米氧化锆粉体为主原料,钒锆蓝色料或Co3O4为着色剂,添加适量烧结助剂制备蓝色氧化锆陶瓷。
5) V-zircon blue pigments
钒-硅酸锆蓝色颜料
6) ZrVFe
锆钒铁
补充资料：钒磷铁矿提钒
钒磷铁矿提钒
extraction of vanadium from the bear vanadium phosphosiderite
和94％。fantintiekuang tifan钒磷铁矿提钒(extraetion of vanadium frombear vanadium phosphosiderite)以含钒磷铁矿为原料制取五氧化二钒的帆提取方法。主要包括钠化焙烧和湿法漫出两道作业。直接用作提饥原料的是含饥磷铁。 含钒磷铁是饥磷铁矿电炉生产单质磷和磷肥的副产品。钒磷铁矿分布在美国爱达荷、蒙大拿、怀俄明、犹他等州，含Pz05 24%~32%、V:O。0.267%~0.625%和少量的铬、镍和钥等。美国克尔麦吉(Kerr-MeGee)化学公司所用的含钒磷铁含饥3.26%~5 .2%、磷24.7%~26.6%、铁59.9%一68.5%、铬3.4%一5.7%、镍。.84%~1%。先将含钒磷铁磨至粒度小于。.42mm，配入1.4倍纯碱和。.1倍的食盐在回转窑中于1043~lo63K温度下焙烧，钒便转变成水溶性的钠盐。熔烧块在加热到沸腾的水中浸出，钒、铬、磷均溶入浸出液。浸出浆液经过滤处理。滤液冷却结晶析出磷酸钠晶体，用离心机分离。晶体中如仍含有钒和铬，可用水重溶后再结晶分离，直到获得合格的磷酸钠(NaaPO;)晶体产品。若Na3PO‘结晶母液含磷高于0. 989/L时则要加入CaclZ，使其生成磷酸钙沉淀，然后水解回收钒。随后往母液中加入硝酸铅，沉淀出铬酸铅。此工艺的钒、铬和磷的回收率分别为85%、65%