1) minimum shrunk rate of flowing section
断面最小收缩比
1.
This paper studied the hydraulic factors of bridge site through the basic hydraulic principles, received bridge site s minimum shrunk rate of flowing section,maximum jammed water depth,and ordinary maximum scouring depth.
据桥位水流图示建立由水力学基本原理表示的方程组 ,通过方程组的分析讨论 ,得出桥位过流断面最小收缩比、最大壅水高度。
2) contracted section
收缩断面
1.
The scope of contracted section,the length of the main current core,the transverse velocity and concentration are given.
分析近区流场和浓度场的特征,得出了下游近区中线流速、浓度和稀释度的沿程变化规律,收缩断面变化范围,以及主流核和高浓度区的长度,也得出了流速和浓度在横断面上的分布状态,并分析和讨论了相对动量、相对扩散器长度对这些特性的影响。
3) section shrinkage
断面收缩
1.
The results show that the pressure loss in the generating process is mainly resulted from the section shrinkage.
结果显示,在超高压水射流形成过程中,压力损失主要是在水流从高压管道进入高压喷嘴时由于流道发生断面收缩而造成的,压力损失大约为最终超高压水射流动能密度的49%;随着喷嘴口径的增大,压力损失减小,整个系统的能量利用率越高;随着水射流压力的增大,压力损失增大,但增大的程度会减小。
4) shrink sector
缩小断面
5) shrinkage on cross section
断面收缩率
1.
According to the testing and studying,ultimate strength,elongation and shrinkage on cross section of two kinds of steel bar were determined.
通过测试研究还得到两种钢筋的极限强度、延伸率和断面收缩率等其他高温力学性能参数。
6) reduction of area
断面收缩率
1.
The brittleness temperature I of Q235G was 1300℃ to melting point and the brittleness temperature III 750~850℃, the range of brittleness temperature III was narrow, and the minimum reduction of area about 48%.
测试结果表明,Q235G钢铸坯的高温强度较小,600℃时抗拉强度约164MPa,屈服强度和抗拉强度均随测试温度降低而增大;铸坯具有良好的塑性,脆性区温度范围较窄,第I脆性温度范围为1300℃至熔点,第III脆性温度范围为750~850℃,在850~1250℃内,该钢种连铸坯的断面收缩率均大于85%。
补充资料：断面收缩率
分子式：
分子量：
CAS号：
性质：材料的塑料性指标之一。材料受拉力断裂时断面缩小，断面缩小的面积与原面积之比值叫断面收缩率，以ψ表示。单位为%。
分子量：
CAS号：
性质：材料的塑料性指标之一。材料受拉力断裂时断面缩小，断面缩小的面积与原面积之比值叫断面收缩率，以ψ表示。单位为%。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条