1) Chelate-forming fibre
螯合形成纤维
2) chelating fiber
螯合纤维
1.
Study on treatment of copper-containing wastewater by super fast chelating fiber with amidocyanogen
胺基型超快螯合纤维处理含铜废水性能研究
2.
Adsorption property of multi-donor atoms chelating fiber for Ag~+
多配位基螯合纤维对Ag~+的吸附性能研究
3.
The thioamide-group chelating fiber was prepared by cross-linking of initial polyacrylonitrile(PAN) fiber with ethylenediamine,and following chemical modification with sodium sulfide.
0%(与缓冲溶液的体积比)、反应时间7 h、反应温度80℃;上述条件下制备得到的螯合纤维对Ag+具有一定的吸附能力,同时具有良好的断裂强度。
3) chelate fiber
螯合纤维
1.
Reaction kinetic study on preparing amidoxime-group chelate fiber;
偕胺肟基螯合纤维制备的反应动力学研究
2.
Preparation of chelate fiber containing amide group Ⅰ. Preparation of precursor fiber;
含氨基螯合纤维的制备 Ⅰ．前驱纤维的制备
3.
Synthesis of PVAAO type chelate fiber and its adsorption for metal ion Cu(Ⅱ);
聚乙烯醇胺肟型螯合纤维的合成及其对铜(Ⅱ)离子的吸附
4) Chelating cellulose
螯合棉纤维
1.
Chelating cellulose is of simple preparation, excellent nature and low cost.
以预处理后的棉纤维为骨架 ,通过间接醚化法 ,接枝合成了 2 巯基苯并螯合棉纤维 (CC MBM ) ,研究了CC MBM吸附重金属离子的动力学行为。
5) Chelating cellulose
螯合纤维素
1.
Chelating cellulose is of simple preparation,excellent nature and low cost.
螯合纤维素制备工艺简单，性能优越，成本低廉。
6) chelata formation
螯合物形成
补充资料：螯合纤维
分子式：
CAS号：
性质：指能与某些金属离子形成螯合物的特种合成纤维。最典型的品种是聚对苯二甲酰草酰双眯腙（PTO）金属螯合纤维，金属离子有锌和钙等，螯合度愈高，模量、热稳定性和抗燃性愈高。以PTO-锌螯合纤维为例，断面呈腰子形，强度2.4cN/dtex,伸长率27%，密度1.7～1.8g/cm3，含湿率14%，190℃×3min的收缩率为1%～2%，极限氧指数87，耐磨性好，但耐酸和耐光性不足；制法是将草酰双脒腙与对苯二甲酰氯缩聚制得PTO，溶于碱水中湿纺，在膨润态下与金属离子螯合而得；用于防火耐热服和绝热材料等。
CAS号：
性质：指能与某些金属离子形成螯合物的特种合成纤维。最典型的品种是聚对苯二甲酰草酰双眯腙（PTO）金属螯合纤维，金属离子有锌和钙等，螯合度愈高，模量、热稳定性和抗燃性愈高。以PTO-锌螯合纤维为例，断面呈腰子形，强度2.4cN/dtex,伸长率27%，密度1.7～1.8g/cm3，含湿率14%，190℃×3min的收缩率为1%～2%，极限氧指数87，耐磨性好，但耐酸和耐光性不足；制法是将草酰双脒腙与对苯二甲酰氯缩聚制得PTO，溶于碱水中湿纺，在膨润态下与金属离子螯合而得；用于防火耐热服和绝热材料等。