Ferrite MgFe2O4 coated carbonyl iron composite powder was prepared by heterogeneous nucleation combined with the liquid deposition method to improve the oxidation resistance performance of carbonyl iron powder.

Al_2O_3 nanosized composite powders encapsulated by ZrO_2(3Y) were prepared by heterogeneous nucleation combined with the co-deposition and were molded by dry pressing.

ZrO_2(3Y)encapsulated Al_2O_3 nano composite powders were prepared by heterogeneous nucleation combined with the liquid co-deposition method using pH buffer solution as precipitator.

Barium titanate based PTC ceramics doped by Nb-Si-Mn heterogeneous nucleation surface deposition method;

Study on the heterogeneous nucleationof CaO/Al2O3/SiO2 system glasses;

For the homogeneous mixing of BaTiO_3(BT) powders with dopants and the exact control of the microstructures,phases and electrical properties of materials,a heterogeneous nucleation method was used to coat dopant Y(OH)_3 on the surface of nano-crystallized hydrothermal BT powders.

The homogeneous nucleation and the non-homogeneous nucleation of argon vapor molecules in the process of condensation were studied by molecular dynamic simulation.

To improve the stability of α-Fe_2O_3 in high temperature application, the SiO_2 and Al_2O_3-coated α-Fe_2O_3 composite particles were prepared from α-Fe_2O_3 coated uniformly with Si(OH)_4 and Al(OH)_3 by heterogeneous nucleation process.

Its hydrolysate ——aluminum hydroxide is coatedon the surface of flaky graphite to improve the wetting property by heterogeneous nucleation process.

Nano-SiC particles were coated with Al(OH) 3 by heterogeneous nucleation process using a buffered pH solution as the precipitating reagent.