Fifty percent scrap steel and fifty percent pig iron infiltrated by flaky graphite were melted in a medium frequency induction furnace for producing synthetic cast iron.

The melting conditions and mechanical properties of the synthetic cast irons produced with steel scrap and returns as main melting charge were introduced.

To resolve the problems above,the synthetic cast iron,i.

The composite brake shoe of cast iron is developed to improve the running speed on existing line.

Development of alloy cast iron standard materials for spectral analysis;

The Cu-Ni alloy cast irons of different chemical constitution were designed,and the corrosion rate in room-temperature concentrated alkaline solution was measured by the static hydrometer method,the microscopics and phase composition of alloy cast iron were observed by optical microscope and XRD.

The corrosion rates of Cu-Ni alloy cast irons in hot concentrated alkaline solution were measured by dynamic condition hydrometer method,the microscopic structures and surface corrosion topographies of alloy cast irons were observed by the optical microscope and SEM,the components were analyzed by XES.

To study high-speed machining process of alloy cast-iron, a finite ele ment model (FEM) is built.