1) Fe/Si multilayers
Fe/Si多层膜
1.
The antiferromagnetic coupling and interface diffusion in Fe/Si multilayers;
Fe/Si多层膜的层间耦合与界面扩散
2.
The antiferromagnetic coupling in Fe/Si multilayers has been observed in 1990s.
早在上世纪九十年代初,人们就观察到Fe/Si多层膜的层间耦合现象。
2) Co/Si multilayer
Co/Si多层膜
3) Si/SiO2 multi-layer films
Si/SiO2多层膜
1.
Si/SiO2 multi-layer films are fabricated using the RF magnetron sputtering technique, and the I-V properties of the multi-layer films are analyzed.
用射频磁控溅射法制备了Si/SiO2多层膜,并对多层膜的I-V特性实验结果进行了拟合。
4) Mo/Si multilayer
Mo/Si多层膜
1.
The beam splitters,which are Mo/Si multilayer deposited o.
采用磁控溅射方法在有效面积为10 mm×10 mm、厚度为100 nm的Si3N4基底上镀制了Mo/Si多层膜,制成了多层膜分束镜。
5) Si/Ge multilayer
Si/Ge多层膜
1.
Photoluminescence of Si/Ge multilayer films deposited by ion-beam sputtering;
溅射Si/Ge多层膜及其发光誊性研究
2.
The Si/Ge multilayers have been prepared by ion beam sputtering technique.
本文采用离子束外延技术制备了一系列的Si/Ge多层膜结构,对样品进行X射线和拉曼散射实验表征。
6) Mo/Si multilayers
Mo/Si多层膜
1.
Mo/Si multilayers prepared with different sputtering power of Mo target;
用不同的Mo靶溅射功率制备Mo/Si多层膜
2.
A series of Mo/Si multilayers were prepared by magnetron sputtering,with top layers being Mo layer and Si layer respectively.
用磁控溅射法分别制备了以Mo膜层和Si膜层为顶层的Mo/Si多层膜系列,利用小角X射线衍射确定了各多层膜的周期厚度。
补充资料：Fe-Si alloy
分子式：
CAS号：
性质：含硅0.5％～4.5％的铁硅合金。为硅在铁中的置换固溶体，属立方晶系。饱和磁感应强度为1.6～1.9J，铁损1～8W/kg。除了冲片使用外，常做成薄带，卷绕成铁芯。采用冷轧或进而热处理的方法获取结构(晶粒定向排列)。电力工业中用于电机、变压器等。电子工业中主要用于电源变压器、磁放大器等。
CAS号：
性质：含硅0.5％～4.5％的铁硅合金。为硅在铁中的置换固溶体，属立方晶系。饱和磁感应强度为1.6～1.9J，铁损1～8W/kg。除了冲片使用外，常做成薄带，卷绕成铁芯。采用冷轧或进而热处理的方法获取结构(晶粒定向排列)。电力工业中用于电机、变压器等。电子工业中主要用于电源变压器、磁放大器等。