1) piezoelectric multilayer film
压电多层膜
5) polyelectrolyte multilayers
聚电解质多层膜
1.
Pristine polyelectrolyte multilayers(PEMs) was prepared by a time-and cost-efficient spin-assisted layer-by-layer(SA-LBL) technique which poly(diallyldimethylammonium chloride) and poly(sodium 4-styrenesulfonate) were sequential droped alternately onto a rotating substrate.
用快速高效的旋涂辅助分子沉积技术在旋转的基底上滴加相反电荷的聚二烯丙基二甲基氯化铵和聚对苯乙烯磺酸钠制备出初始聚电解质多层膜(PEMs),在PEMs上吸附Cu2+然后于硼氢化钠溶液中还原,通过9次吸附-还原循环,在PEMs内原位生成Cu纳米微粒,构成Cu纳米微粒掺杂的聚电解质多层膜。
2.
The fabrication of micro-structures on polymer surfaces has been fulfilled via patterned compression of polyelectrolyte multilayers (PEMs) and thermal pressing method (TPM) respectively.
本文分别利用聚电解质多层膜的压缩和热压技术两种方法构建了聚合物微结构。
6) multilayer ferroelectric thin film
多层铁电薄膜
1.
Structural design and preparation of BIT/PLZT/BIT multilayer ferroelectric thin film;
BIT/PLZT/BIT多层铁电薄膜结构设计及制备的实验研究
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。