1) perpenticular magnetic anisotropy
垂直膜面各向异性
2) perpendicular anisotropy
垂直各向异性
1.
All the samples show strong perpendicular anisotropy and the perpendicular coercivity(H_(c⊥)) reaches the maximum 138kA/m as x=11nm.
样品垂直方向的矫顽力在x=11nm时达到最大,为138kA/m,平行于膜面方向的矫顽力基本上与x的变化无关,且所有的样品都显示出很强的垂直各向异性。
2.
The nano-multilayer films have large perpendicular anisotropy and high coercive force than the TbDyFe single layer film, and show giant magnetostrietive effect though they have perpendicular anisotropy.
尽管纳米多层膜样品具有垂直各向异性,但仍具有超磁致伸缩性能。
3.
The Co/Pt multilayers with perpendicular anisotropy are the potential and promising elements in design of perpendicular high density storage media, It have stimulated increasing interests.
具有垂直各向异性的Co/Pt多层膜作为很有发展前景的垂直磁记录介质,引起了人们的研究兴趣。
3) perpendicular magnetic anisotropy
垂直磁各向异性
1.
The results show that sputtering Ar gas pressure has a great effect on the microstructure, perpendicular magnetic anisotropy and the coercivity of [Co 85 Cr 15 /Pt] 20 multilayers.
研究结果表明 ,Ar溅射气压对 [Co85Cr1 5 Pt]2 0 多层膜的微结构、垂直磁各向异性和矫顽力有重要的影响 。
2.
The results show that the nanowire arrays are amorphous with a perpendicular magnetic anisotropy and high coercivity H_c=3.
利用x射线衍射仪、透射电子显微镜、振动样品磁强计和穆斯堡尔谱仪研究了样品的结构和磁性,发现纳米线阵列是非晶结构,且拥有垂直磁各向异性和高的矫顽力,Hc=3·04×104A/m。
3.
And the origin of the perpendicular magnetic anisotropy in these films was studied.
理论分析结果表明 ,TbCo非晶垂直磁化膜的垂直磁各向异性主要来自于Tb离子的非球对称分布电荷与膜内晶场之间的库仑相互作用以及膜内的应力。
4) perpendicular magnetic anisotropy
垂直各向异性
1.
In this paper, we report the observation of exchange bias in (Pt/Co)-n/FeMn multilayer with perpendicular magnetic anisotropy.
采用磁控溅射方法制备了以Pt为缓冲层和保护层的具有垂直各向异性(Pt/Co)n/FeMn多层膜。
5) Vertical anisotropy
垂直各向异性
1.
The results show that high magnetic performance CoNiMnP permanent magnet films with vertical anisotropy could be fabricated with electric current density less than 10mA/cm2 and pH 3～4 at room temperature.
采用电镀法制备了与微电子CMOS工艺兼容的硅基CoNiMnP垂直各向异性永磁薄膜,并对该薄膜的微结构、组成、磁性能等进行了分析与测试。
2.
The results show that high magnetic performances CoNi 1-x Nd x MnP permanent magnet films with vertical anisotropy can be fabricated with current density less than 10 mA·cm -2 at room temperature.
2mm的硅片上设计并制备了 2 0 0 0个大小为 5 0 μm× 5 0 μm的CoNi1 -xNdxMnP垂直各向异性永磁薄膜阵列 ,并对该薄膜陈列的组成、磁性能等进行了分析与测试。
6) Anisotropic surface film
各向异性表面膜
补充资料：各向同性和各向异性
物理性质可以在不同的方向进行测量。如果各个方向的测量结果是相同的,说明其物理性质与取向无关,就称为各向同性。如果物理性质和取向密切相关，不同取向的测量结果迥异，就称为各向异性。造成这种差别的内在因素是材料结构的对称性。在气体、液体或非晶态固体中，原子排列是混乱的,因而就各个方向而言,统计结果是等同的，所以其物理性质必然是各向同性的。而晶体中原子具有规则排列，结构上等同的方向只限于晶体对称性所决定的某些特定方向。所以一般而言，物理性质是各向异性的。例如， α－铁的磁化难易方向如图所示。铝的弹性模量E沿[111]最大(7700kgf/mm2),沿[100]最小(6400kgf/mm2)。对称性较低的晶体（如水晶、方解石）沿空间不同方向有不同的折射率。而非晶体(过冷液体)，其折射率和弹性模量则是各向同性的。晶体的对称性很高时，某些物理性质(例如电导率等)会转变成各向同性。当物体是由许多位向紊乱无章的小单晶组成时，其表观物理性质是各向同性的。一般合金的强度就利用了这一点。倘若由于特殊加工使多晶体中的小单晶沿特定位向排列（例如金属的形变"织构"、定向生长的两相晶体混合物等），则虽然是多晶体其性能也会呈现各向异性。硅钢片就是这种性质的具体应用。
介于液体和固体之间的液晶，有的虽然分子的位置是无序的，但分子取向却是有序的。这样，它的物理性质也具有了各向异性。
介于液体和固体之间的液晶，有的虽然分子的位置是无序的，但分子取向却是有序的。这样，它的物理性质也具有了各向异性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条