1) Co-Ni alloy nanowires
Co-Ni合金纳米线
2) nanocrystalline Co-Ni
纳米晶Co-Ni合金
1.
The nanocrystalline Co-Ni alloys were prepared by jet electrodeposition in the nickel chloride and cobalt sulfate bath containing additive and the cathodic polarization curves of Co-Ni alloys were measured.
在氯化镍-硫酸钴体系电解液中采用添加剂喷射电沉积纳米晶Co-Ni合金,测定了其阴极极化曲线。
3) bulk nanocrystaline Co-Ni alloy
块体纳米晶Co-Ni合金
4) La-Co alloy nanowires
La-Co合金纳米线
5) Ni-Mo alloy nanowire
Ni-Mo合金纳米线
1.
Ni-Mo alloy nanowires were prepared using porous anodic alumina(PAA) as templates and were characterized by SEM and XPS.
使用多孔阳极氧化铝模板,电沉积制备了Ni-Mo合金纳米线。
6) Ni-Co alloy
Ni-Co合金
1.
A Study on Electrodeposition of Ni-Co Alloy and Structure of Deposit;
电沉积Ni－Co合金及其结构研究
2.
Microstructures and mechanical properties of pulsed electrodeposition nanocrystalline Ni-Co alloy;
脉冲电沉积纳米晶Ni-Co合金的组织结构与力学性能
3.
By the method of high frequency pulse electroplating, Ni-Co alloy coating was prepared.
采用高频脉冲电流,制备Ni-Co合金镀层。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)