1) surface acid sites
表面酸位
1.
The surface acid sites of diatomite detected by pyridine-Raman spectrometry;
运用吡啶吸附-拉曼光谱探测硅藻土表面酸位
2) acid and basic site on solid surface
固体表面酸碱位
3) surface acid-base potentiometric titration
表面酸碱电位滴定
4) Zeta potential
表面电位
1.
By means of Zeta potential tests on the surface of cement particles with different addition of naphtha- lene sulphonate-based superplasticizer(UNF-5) and co-polycarboxylate-based superplasticizer(COPOCA202) as well as tests of zeta potential varied along with time on the surface of cement particles with saturated addition of superplasticizer and without addition of superp.
文章通过不同掺量萘系(UNF-5)和聚羧酸系(COPOCA202)超塑化剂的水泥颗粒表面电位试验和此两种超塑化剂饱和掺量以及未掺超塑化剂时水泥颗粒表面电位随时间变化试验,认为:超塑化剂的掺入使水泥颗粒电性统一,掺UNF-5带负电,掺COPOCA202则带正电,并随时间的延长其绝对值均逐渐降低;这种电性统一是新拌水泥浆体分散的重要来源;COPOCA202系比UNF-5对表面电位改变能力小。
2.
X-ray photoelectron spectroscopy,Ultraviolet-visible spectrophotometry,zeta potential and electrochemical workstation were used to study the inhibiting-mechanism of BTA.
利用柠檬酸体系抛光液研究了苯并三氮唑(BTA)缓蚀剂对铜化学机械抛光过程和抛光效果的影响,并通过X射线光电子能谱仪、紫外可见吸收光谱仪及表面电位测试和电化学分析等手段分析了抛光液中BTA缓蚀剂在铜化学机械抛光过程中的作用机理。
3.
It is found that superplasticizer perhaps adsorb on the cement particles unevenly, that changing zeta potential capacity of COPOCA202 is smaller than UNF-5, and that COPOCA202 can destroy flocculation structure more thoroughly but there are also flocculation s.
本文通过超塑化剂在水泥颗粒表面的吸附试验、动电试验以及流变试验,研究了超塑化剂在水泥颗粒表面上的吸附特征、掺超塑化剂后的动电性质以及其对新拌水泥浆体结构的破坏特性,发现超塑化剂在水泥颗粒表面上的吸附可能是不均匀的,聚羧酸系超塑化剂(COPOCA202)对表面电位改变能力较萘系(UNF-5)的低,COPOCA202对絮凝结构的破坏能力较UNF-5大,并且即掺如COPOCA202浆体中还存在有絮凝结构,从而推断新拌水泥浆体中各个絮凝结构强度不均一。
5) Surface coordination
表面配位
6) surface site
表面位
1.
In this paper,the surface sites of quartz and their protonation were first analyzed and discussed,and then the surface reaction of heavy metal ions,involving Cu 2+ ,Pb 2+ ,Cd 2+ and Ni 2+ ,with quartz were completely investigated.
矿物表面因存在有各种悬空键 ,而形成了表面活性官能团 ,称作“表面位”。
2.
The surface sites of tripoli (α-quartz) and its protonation are first analyzed and discussed, and then the surface electrochemical properties of tripoli are further investigated.
分析与探讨了粉石英的表面位及其质子化反应 ,对粉石英的表面电化学性质作了进一步研究。
补充资料：固体表面酸碱位
分子式：
CAS号：
性质：氧化物和混合氧化物类固体酸碱(如，氧化铝、氧化锌、二氧化钛、氧化镁、氧化锆、氧化钙、氧化铝-二氧化硅、二氧化硅-氧化镁等)在不同处理条件下产生酸性及碱性中(位)。如氧化铝水合物脱水可产生L酸中心及碱中心，L酸中心吸水又可成为B酸中心。固体表面酸碱中心是异构化、裂解、烷基化、水合、脱水等固体酸碱催化反应的活性中心。
CAS号：
性质：氧化物和混合氧化物类固体酸碱(如，氧化铝、氧化锌、二氧化钛、氧化镁、氧化锆、氧化钙、氧化铝-二氧化硅、二氧化硅-氧化镁等)在不同处理条件下产生酸性及碱性中(位)。如氧化铝水合物脱水可产生L酸中心及碱中心，L酸中心吸水又可成为B酸中心。固体表面酸碱中心是异构化、裂解、烷基化、水合、脱水等固体酸碱催化反应的活性中心。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条