1) hardening exponent
硬化指数
1.
The hardening exponent,value of plastic strain ratio,yield strength,tensile strength,even percentage elongation and other mechanical performances have been studied.
对400MPa超级钢板材进行了拉伸试验、冷弯试验和金相组织检验,获得了超级钢板的硬化指数、塑性应变比、屈服强度、极限强度等力学性能,并分析了400MPa超级钢板的冲压成形性能,了解这些性能对超级钢冲压件在汽车行业里的应用与生产具有一定的指导作用。
2.
It is simple and effective to calculate the hardening exponent(n-value) for steel sheet using the testprogram composed with Testware-SX software module and data processing program composed with macro-instruction.
用Testware—SX软件模块编制试验程序,宏命令编制数据处理程序计算薄板硬化指数n值,该方法简单有效。
2) activation index
活化指数
1.
The surface modification degree is characterized by the activation index.
采用2种钛酸酯偶联剂用量体系(小用量和大用量)对纳米氧化锌进行表面改性,并用活化指数表征改性效果。
2.
Heavy calcium carbonate(HCC) was modified by titanate coupling agent NDZ-311 in isopropyl alcohol by means of ultrasonic dispersion,the activation index was up to 98.
采用异丙醇溶解的钛酸酯偶联剂NDZ-311对重钙进行超声湿法表面改性,改性后重钙粉体的活化指数达最大值98。
3.
Influences of surfactant dosages,modification time,modification temperature,initial slurry concentration,stirring rate and drying temperature are investigated,and activation index and contact angle are used to evaluate medication effect.
采用几种改性剂对碳酸钙晶须进行了表面改性试验,结果表明硬脂酸钠对碳酸钙晶须的改性效果显著,以硬脂酸钠为改性剂,考察了改性剂用量、改性时间、改性温度、初始料浆质量分数、搅拌速度、烘干温度等因素对碳酸钙晶须表面改性的影响,选择活化指数及接触角对碳酸钙晶须的改性效果进行表征,在最佳试验条件下,改性产品的活化指数为100%,接触角为146。
3) activity index
活化指数
1.
Taking activity index and pH value as targets,when coupling agent-styrene were acted as grafting surface treatment agent,the modification effects of nano aluminum nitride powder was researched by varying dosage of surface treatment agents,processing temperature and time.
以活化指数和pH值为考核指标,通过变化改性剂的用量、处理温度以及处理时间等,研究了偶联剂–苯乙烯接枝改性剂对纳米AlN粉末的表面改性效果。
4) hardening index
硬化指数
1.
The mechanical performances such as hardening index,value of plastic strain ratio,yield stre.
研究了超级钢板的硬化指数、塑性应变比、屈服强度、极限强度、均匀延伸率等机械性能,并分析了超级钢板的冲压成形性能,超级刚具有较好的胀形性能、拉深性能、弯曲性能,抗起皱性能等冲压性能,可以广泛地应用于汽车冲压零件生产中。
2.
In this thesis, by using micro- and nano- indentation methods and uniaxial compression test, the plastic deformation behavior of several BMG systems was investigated, focusing on the physical nature of the pressure sensitivity index and the strain hardening index of the BMGs.
重点研究了非晶合金的压力敏感性(pressure sensitivity),探讨了其压力敏感因子和硬化指数的物理本质及其影响因素;分析了具有不同压力敏感因子的非晶合金的剪切带形貌与演变规律;研究了玻璃转变温度,结构弛豫对非晶变形的影响;初步研究了非晶的挤压变形行为。
5) active ratio
活化指数
1.
In this research,the active ratio of modified flying-ash reaches over 95%.
以上海市生活垃圾焚烧飞灰的高附加值资源化和稳定化为目标,初步研究茶皂素对城市生活垃圾焚烧飞灰改性活化以及对重金属离子的螯合效果,改性飞灰的活化指数可达95%以上。
2.
Based on the indexes of active ratio and analysis of IR-spectrometer, the active ratio of ACS1 modified fly ash can be found higher than 95% under the condition of surfactant dosage at 7.
通过活化指数和红外光谱分析,在改性剂用量7·0mL/100g飞灰、改性时间15min和改性温度75℃的条件下,ACS1改性飞灰的活化指数可达95%以上。
3.
Primary thermal decomposition temperature of the retardant is up to or more than 260℃,and its active ratio is about 95%.
本文采用两步法,经过表面多层包覆改性及无机-有机多层包覆改性处理,制备出一种铝基复合阻燃剂,使其初始分解温度达到260℃以上,活化指数达到90%。
6) strain-hardening exponent
硬化指数
1.
The nominal yield ratio(σ_s/σ_b),true stress yield ratio(S_s/S_b) and strain-hardening exponent(n) of five kinds of steel were derived from tensile experiments.
试验测算出X80、X65、X60、X46、Q235等五种材料的名义应力屈强比sσ/bσ和真实应力屈强比Ss/Sb及硬化指数n。
补充资料：硬化指数
硬化指数
hardening index
y inghua zhishu硬化指数(hardening index)指金属薄板成形时真应力S一真应变。关系式S~K广中的幕指效城式中K为强度系数)。亦即双对数坐标系场~坛。中，真应力一真应变关系式195~坛K十滋g。直线的抖率。是无量纲值，又称加工硬化指数。(见真应力一宾应变曲线)从数值上看，硬化指数，值等于(或近似等于)单向拉伸时材料最大均匀伸长应变的大小，即所渭细颈点应变。应变分布不均是板材成形中的一个重要特点，，值的大小实际上反映了板材的应变均化能力，主要说明: (1)成形件的应变峰值不同。n值小的材料产生的应变峰值高，，值大的材料产生的应变峰值低; (z)成形件上的应变分布不同。n值小的材料应变分布不均匀，n值大的材料应变分布均匀。 硬化指数n值对板材成形极限曲线具有明显的影响，n值大材料的成形极限曲线高，n值小材料的成形极限曲线低。板材的拉胀性能在很大程度上取决于材料的n值，。值高时，拉胀性能也好。因此，硬化指数，值是评价板材成形性能的重要指标之一。 (康永林)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。