In this study,Al-30Si and Al-40Si hypereutectic high-silicon aluminum alloy were fabricated with a method in which air-atomization was followed by vacuum canning hot-extrusion process.
针对应用广泛的低密度、低膨胀、高热导、高比强的高硅铝合金,采用空气雾化水冷与真空包套热挤压工艺相结合的方法,制备了Al-30Si与Al-40Si过共晶高硅铝合金材料,并通过金相微观组织分析、力学性能检测及拉伸试样断口扫描,研究了不同热挤压温度对合金的组织形貌与性能的影响。
2.
Light weight Al-30Si and Ai-40Si used for e ectronic packaging in the aviation and space-flight are fabricated with a method in which air-atomization is followed by vacuum canning hot-extrusion process.
针对航空航天电子封装用轻质高硅铝合金材料,采用空气雾化水冷与真空包套热挤压工艺相结合的方法,制备了 Al-30Si 和 Al-40Si 过共晶高硅铝合金材料,并通过金相显微镜观察了材料的微观组织,测定了合金材料的抗拉强度以及延伸率,对拉伸试样的断口进行了扫描。
3.
Hypereutectic high-silicon aluminum alloy(Al-30Si and Al-40Si)was fabricated with a method in which air-atomization was followed by vacuum canning hot-extrusion process.
采用空气雾化水冷与真空包套热挤压工艺相结合的方法,制备了Al 30Si和Al 40Si过共晶高硅铝合金材料,采用扫描电镜与金相显微镜进行了显微组织分析,检测了其力学性能。