1) unidirectional continuous bamboo fiber reinforced polymer
连续竹纤维增强聚合物
1.
The workmanship and process of unidirectional continuous bamboo fiber reinforced polymer (BFRP)specimens were described, and the experimental study on the tensile mechanical properties of BFRP was conducted.
描述了一种单向连续竹纤维增强聚合物试件的制作工艺过程:研究了该型竹纤维增强复合材料的拉伸力学性能。
2) unidirectional continuous E-glass fiber reinforced polymer
连续玻璃纤维增强聚合物
1.
The test results were compared with those of unidirectional continuous E-glass fiber reinforced polymer(GFRP)composite.
将该性能与单向连续玻璃纤维增强聚合物的拉伸力学性能进行了比较,发现竹纤维增强聚合物的拉伸模量要明显高于玻璃纤维增强聚合物的对应值,而其拉伸强度和玻璃纤维增强聚合物的相当。
3) fiber reinforced polymer
纤维增强聚合物
1.
Fiber orientation and stress analysis for fiber reinforced polymeric melt;
纤维增强聚合物熔体的纤维取向和流场应力分析
2.
Numerical simulation of non-isothermal flow of fiber reinforced polymeric melt;
纤维增强聚合物熔体的非等温流动数值模拟
3.
Particular atten- tion is paid to the application of the fiber reinforced polymer.
综述了管道修复用复合材料的研究进展,重点介绍了以纤维增强聚合物(FRP)为主体的管道修复材料及相关技术的进展。
4) continuous glass fiber reinforced PP composite
连续纤维增强聚丙烯复合材料
6) continuing fibre-strengthened TMCS
连续纤维增强TMCS
补充资料：玻璃纤维增强液晶聚合物
分子式：
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条